Abstract:C/C-ZrC-SiC composites were prepared by reactive melt infiltration and tested using an oxyacetylene torch with the heat fluxes of 4.18 and 2.38 MW/m(2). The results showed that compared to C/C and C/C-SiC at the heat flux of 4.18 MW/m(2), the mass ablation rates of C/C-ZrC-SiC were decreased by 60.8% and 44.8%, respectively. Its linear ablation rate was 7.3% higher than that of C/C, but was 13.5% lower than that of C/C-SiC. The C-SiC matrix and fibers of C/C-SiC in the center region were severely depleted by the high ablation temperature. C/C-ZrC-SiC composites experienced the temperature exceeding 2400 degrees C associated with intense mechanical scouring of gas flow. The severe depletion of SiC and carbon fibers on the surface led to the formation of the porous ZrO2 layer. The spallation of ZrO2 occurred in the center of the ablated surface as a result of mechanical denudation of high temperature gas flow. At the heat flux of 2.38 MW/m(2), the mass and linear ablation rates of C/C-ZrC-SiC were decreased by 76.8% and 88.4% (C/C), 66.9% and 58.3% (C/C-SiC), respectively. The oxide was slightly peeled off in the center region of C/C-SiC. The surface temperatures of C/C-SiC and C/C-ZrC-SiC were lower than that of C/C composites. The island-like ZrO2 and SiO2 layer were formed on the ablated surface of C/C-ZrC-SiC and acted as effective barriers to shield the ablation heat and slow inward transport of oxygen to the underlying material.

Effects of Oxidizing Species on Ablation Behavior of C/C-Zrb2-Zrc-Sic Composites Prepared by Precursor Infiltration and Pyrolysis

Ablation Behavior and Mechanism of C/C–ZrC–SiC Composites under an Oxyacetylene Torch at 3000°C

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

Improved Ablation Resistance of C/Sic-Zrb2 Composites Via Polymer Precursor Impregnation and Pyrolysis

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch

Mechanical Properties and Ablation Behavior of C/C-ZrC and C/C-ZrC-SiC Composites Prepared by Precursor Infiltration and Pyrolysis Combined with Chemical Vapor Infiltration

Ablation Properties of C/C-Zrc-Sic Composites by the Precursor Infiltration Pyrolysis

Ablation Behavior of C/C-ZrC-SiC Composites Prepared by Reactive Melt Infiltration under Oxyacetylene Torch at Two Heat Fluxes

Ablation Performances of Multi-Phased C/C-Zrc-Sic Ultra-High Temperature Composites

Ablation Resistance of Different Coating Structures for C/ZrB2–SiC Composites under Oxyacetylene Torch Flame

Ablation Behavior of a C/C-ZrC-SiC Composite Based on High-Solid-loading Slurry Impregnation under Oxyacetylene Torch

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Ablation Behavior of ZrC–SiC Coated C/C–ZrC–SiC Composites Prepared by Precursor Infiltration Pyrolysis Combined with Reactive Melt Infiltration

Ablation Behavior of Sharp-Shape C/C-SiC-ZrB2 Composites under Oxyacetylene Flame

Effect of ZrC–SiC Content on Microstructure and Ablation Properties of C/C Composites

Ablation Performance of C/C-ZrC-SiC Composites with In-Situ YSi2-doped ZrC-SiC-ZrSi2 Coating under Oxyacetylene Torch

Ablative and Mechanical Properties of C/C–ZrC Composites Prepared by Precursor Infiltration and Pyrolysis Process

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch