Abstract:C/C-ZrC-SiC composites were prepared by reactive melt infiltration and tested using an oxyacetylene torch with the heat fluxes of 4.18 and 2.38 MW/m(2). The results showed that compared to C/C and C/C-SiC at the heat flux of 4.18 MW/m(2), the mass ablation rates of C/C-ZrC-SiC were decreased by 60.8% and 44.8%, respectively. Its linear ablation rate was 7.3% higher than that of C/C, but was 13.5% lower than that of C/C-SiC. The C-SiC matrix and fibers of C/C-SiC in the center region were severely depleted by the high ablation temperature. C/C-ZrC-SiC composites experienced the temperature exceeding 2400 degrees C associated with intense mechanical scouring of gas flow. The severe depletion of SiC and carbon fibers on the surface led to the formation of the porous ZrO2 layer. The spallation of ZrO2 occurred in the center of the ablated surface as a result of mechanical denudation of high temperature gas flow. At the heat flux of 2.38 MW/m(2), the mass and linear ablation rates of C/C-ZrC-SiC were decreased by 76.8% and 88.4% (C/C), 66.9% and 58.3% (C/C-SiC), respectively. The oxide was slightly peeled off in the center region of C/C-SiC. The surface temperatures of C/C-SiC and C/C-ZrC-SiC were lower than that of C/C composites. The island-like ZrO2 and SiO2 layer were formed on the ablated surface of C/C-ZrC-SiC and acted as effective barriers to shield the ablation heat and slow inward transport of oxygen to the underlying material.

Ablative and Mechanical Properties of C/C–ZrC Composites Prepared by Precursor Infiltration and Pyrolysis Process

Mechanical Properties and Ablation Behavior of C/C-ZrC and C/C-ZrC-SiC Composites Prepared by Precursor Infiltration and Pyrolysis Combined with Chemical Vapor Infiltration

Ablation Properties of C/C-Zrc-Sic Composites by the Precursor Infiltration Pyrolysis

Ablation Properties of C/C-ZrC-SiC Composites

Ablation Behavior of ZrC–SiC Coated C/C–ZrC–SiC Composites Prepared by Precursor Infiltration Pyrolysis Combined with Reactive Melt Infiltration

Effects of Oxidizing Species on Ablation Behavior of C/C-Zrb2-Zrc-Sic Composites Prepared by Precursor Infiltration and Pyrolysis

Ablation Behavior and Mechanism of C/C–ZrC–SiC Composites under an Oxyacetylene Torch at 3000°C

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Ablation Behavior of a C/C-ZrC-SiC Composite Based on High-Solid-loading Slurry Impregnation under Oxyacetylene Torch

C/C–ZrC Composite Prepared by Chemical Vapor Infiltration Combined with Alloyed Reactive Melt Infiltration

Reaction kinetics and ablation properties of C/C–ZrC composites fabricated by reactive melt infiltration

Mechanical Property, Oxidation and Ablation Resistance of C/C–ZrB2–ZrC–SiC Composite Fabricated by Polymer Infiltration and Pyrolysis with Preform of Cf/ZrB2

Zirconium Carbide Skeleton Reinforced Pyrocarbon Composites with Tunable Mechanical Strength, Thermophysical Properties and Ablation Resistance

Microstructure and Mechanical Performance Evolution of C/C–ZrC Composites Exposed to Oxyacetylene Flame

Preparation and properties of C/C-ZrC-SiC-ZrB2 composites via polymer infiltration and pyrolysis

Ablation Behavior of C/C-ZrC-SiC Composites Prepared by Reactive Melt Infiltration under Oxyacetylene Torch at Two Heat Fluxes

Ablation Property and Mechanism of ZrC-Cu-C/C Composites

Microstructure and Ablation Property of C/C-ZrC Composites Manufactured by Reactive Melt Infiltration

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Ablation Performances of Multi-Phased C/C-Zrc-Sic Ultra-High Temperature Composites

Effects of precursor concentration on the microstructure and properties of ZrC modified C/C composites prepared by precursor infiltration and pyrolysis