Abstract:The microstructures, mechanical properties, and ablation behaviors of carbon-fiber reinforced carbon and ZrC–SiC ceramic matrix composites (C/C–ZrC–SiC) fabricated through reactive melt infiltration were systematically researched, of which preforms were densified using different substrate carbon: (i) resin carbon (RdC) and (ii) pyrolitic carbon (PyC) for comparison. The results showed that the densification process with pores that differ in location and size dominated the distribution of ceramic phases within pristine carbon-fiber reinforced carbon (C/C). In addition, the C/C–ZrC–SiC samples with different carbon substrates possessed different mechanical properties. The flexural strength of the C/PyC-ZrC-SiC composites was significantly higher, exhibiting a ductile fracture behavior, which is different from that of the brittle fracture model in C/RdC-ZrC-SiC composites. However, after being exposed to an oxyacetylene ablation torch at 2500 °C for 30–240 s, the C/RdC-ZrC-SiC composites exhibited better ablation resistances because there were more carbon matrix and carbide blocks per unit volume in the composites, and the structure of C/RdC-ZrC-SiC possessed a shorter healing time for pores during ablation. In other words, an integrated oxide scale on the ablated surface can be formed in a relatively shorter time. Therefore, the superior ablation behavior can largely be ascribed to the formation of dense oxides containing molten-like SiO2, which could effectively resist scouring and seal the pores promptly during ablation.

Microstructure and Ablation Property of C/C-ZrC Composites Manufactured by Reactive Melt Infiltration

Reaction kinetics and ablation properties of C/C–ZrC composites fabricated by reactive melt infiltration

Ablation Property and Mechanism of ZrC-Cu-C/C Composites

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Microstructure and Ablation Behavior of Carbon/carbon Composites Infiltrated with Zr–Ti

Influence of Reactive Melt Infiltration Parameters on Microstructure and Properties of Low Temperature Derived Cf/ZrC Composites

Microstructure and Ablation Property of a Carbon/Carbon–ZrC Composite Fabricated by Reactive Melt Infiltration with Zr/Cu Powder Mixture

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Effects of Porous C/C Density on the Densification Behavior and Ablation Property of C/C–ZrC–SiC Composites

Microstructures and Ablation Properties of C/C−SiC−ZrC Composites Prepared Using C/C Skeletons with Various Densities

Ablation Properties of C/C-ZrC-SiC Composites

Ablative and Mechanical Properties of C/C–ZrC Composites Prepared by Precursor Infiltration and Pyrolysis Process

Ablation Behavior of ZrC–SiC Coated C/C–ZrC–SiC Composites Prepared by Precursor Infiltration Pyrolysis Combined with Reactive Melt Infiltration

Microstructure and ablation properties of Si-Mo-Zr modified C/C composites by reactive melt infiltration

The Ablation Behavior and Mechanical Property of C/C-SiC-ZrB2 Composites Fabricated by Reactive Melt Infiltration

Microstructure and ablation behavior of C/C composites doped with ZrB2

Mechanical Properties and Ablation Behavior of C/C-ZrC and C/C-ZrC-SiC Composites Prepared by Precursor Infiltration and Pyrolysis Combined with Chemical Vapor Infiltration

The Microstructure, Ablative Resistance and Mechanical Properties of C/C-(Zr, V, Si)C Composites after Ablation

Comparative Insights into C/C–ZrC–SiC Composites with Different Substrate Carbon on Microstructures, Mechanical Properties, and Ablation Behaviors

C/C–ZrC Composite Prepared by Chemical Vapor Infiltration Combined with Alloyed Reactive Melt Infiltration

Ablation Behaviour and Mechanical Performance of ZrB2-ZrC-SiC Modified Carbon/carbon Composites Prepared by Vacuum Infiltration Combined with Reactive Melt Infiltration