Microstructure and ablation behavior of C/C composites doped with ZrB2

Huihui Sun,Hejun Li,XueTao Shen,Gaoxiang Cao,Xinfa Qiang,XiaoBin Ren,Qiangang Fu
DOI: https://doi.org/10.3724/SP.J.1077.2011.10918
IF: 1.292
2011-01-01
Journal of Inorganic Materials
Abstract:ZrB2 was first introduced into carbon preforms through ultrasonic and vacuum immersion-carbonthermal reduction method. After densification using thermal gradient chemical vapor infiltration and graphitization, ZrB2 doped C/C composites were prepared. The oxyacetylene ablation results show that the linear and mass ablation rates of the composites after doping with 6.87wt% ZrB2 decreased by 64.9% and 67.5%, respectively. The ablation of C/C composites is mainly controlled by thermochemical and thermophysical reactions and mechanical denudation does not play a dominant role. The evaporation of ZrO2/B2O3 during ablation would take away large amounts of heat, reducing the thermal impact of flame to the ablation surface.