Abstract:Reactive melt infiltration (RMI) has been proved to be one of the most promising technologies for fabrication of C/SiC composites because of its low cost and short processing cycle. However, the poor mechanical and anti-ablation properties of the RMI-C/SiC composites severely limit their practical use due to an imperfect siliconization of carbon matrixes with thick walls and micron-sized pores. Here, we report a high-performance RMI-C/SiC composite fabricated using a carbon fiber reinforced nanoporous carbon (NC) matrix preform composed of overlapping nanoparticles and abundant nanopores. For comparison, the C/C performs with conventional pyrocarbon (PyC) or resin carbon (ReC) matrixes were also used to explore the effect of carbon matrix on the composition and property of the obtained C/SiC composites. The C/SiC derived from C/NC with a high density of 2.50 g cm -3 has dense and pure SiC matrix and intact carbon fibers due to the complete ceramization of original carbon matrix and the almost full consumption of inspersed silicon. In contrast, the counterparts based on C/PyC or C/ReC with a low density have a little SiC, much residual silicon and carbon, and many corroded fibers. As a result, the C/SiC from C/NC shows the highest flexural strength of 218.1 MPa and the lowest ablation rate of 0.168 μm s -1 in an oxyacetylene flame of ~ 2200 °C with a duration time of 500 s. This work opens up a new way for the development of high-performance ceramic matrix composites by siliconizing the C/C preforms with nanoporous carbon matrix

Fabrication and properties of 2D C/C-ZrB2-ZrC-SiC composites by hybrid precursor infiltration and pyrolysis

Mechanical and ablation properties of 3D orthogonal woven C/C-SiC composite based on high-solid-loading slurry impregnation

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

ZrC Modified Carbon/carbon Composites Using ZrSi2 and Zr-Cu Alloys As Reactive Infiltrating Materials: A Comparative Investigation

Ablation behaviour of Csf/ZrB2-SiC composites fabricated by direct ink writing and reactive melt infiltration

Construction of sandwich-structured C/C-SiC and C/C-SiC-ZrC composites with good mechanical and anti-ablation properties

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Microstructure evolution and ablation mechanisms of Csf/ZrB2-SiC composites at different heat fluxes under air plasma flame

Architectural Engineering Inspired Method of Preparing C-f/ZrC-SiC with Graceful Mechanical Responses

Fabrication and microstructure evolution of Csf/ZrB2-SiC composites via direct ink writing and reactive melt infiltration

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Preparation and Properties of C/SiC Composites Reinforced by High Thermal Conductivity Graphite Films

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

Ablation behavior of La 2 O 3 modified C/C–ZrC composites fabricated by precursor infiltration and pyrolysis

Ablation of advanced C/C-ZrC-SiC leading edge composites

Preparation, Mechanical and Ablation Properties of a C/C-TaB2-SiC Composite

Microstructure and ablation behaviour of C/C-SiC-ZrC-Cu composites prepared by reactive melt infiltration

Fabrication of (SiC-AlN)/ZrB2 Composite with Nano-Micron Hybrid Microstructure via PCS-Derived Ceramics Route

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch