Abstract:A novel segmented control strategy for selenization environment is introduced to regulate the selenization reaction by controlling the evaporation area of Se. This selenization method helps to promote element homogenization, optimize surface smoothness, and obtain a high‐crystalline‐quality absorber with low‐point defects. And the CZTSSe solar cell with a PCE of 13.77% is successfully achieved. High‐crystalline‐quality absorbers with fewer defects are crucial for further improvement of open‐circuit voltage (VOC) and efficiency of Cu2ZnSn(S,Se)4 (CZTSSe) solar cells. However, the preparation of high‐quality CZTSSe absorbers remains challenging due to the uncontrollability of the selenization reaction and the complexity of the required selenization environment for film growth. Herein, a novel segmented control strategy for the selenization environment, specifically targeting the evaporation area of Se, to regulate the selenization reactions and improve the absorber quality is proposed. The large evaporation area of Se in the initial stage of the selenization provides a great evaporation and diffusion flux for Se, which facilitates rapid phase transition reactions and enables the attainment of a single‐layer thin film. The reduced evaporation area of Se in the later stage creates a soft‐selenization environment for grain growth, effectively suppressing the loss of Sn and promoting element homogenization. Consequently, the mitigation of Sn‐related deep‐level defects on the surface and in the bulk induced by element imbalance is simultaneously achieved. This leads to a significant improvement in nonradiative recombination suppression and carrier collection enhancement, thereby enhancing the VOC. As a result, the CZTSSe device delivers an impressive efficiency of 13.77% with a low VOC deficit.

Effects of Selenization on Phase Transition and S/(S+Se) Ratios of As-Deposited Cu2ZnSnS4 Absorbers Sputtered by a Quaternary Target

An investigation on phase transition for as-sputtered Cu 2 ZnSnSe 4 absorbers during selenization

Formation of Alloyed Cu2CoxZn1-xSn(S,Se)4 Absorption Layer and Its Application in Solar Cells.

Effects of Selenium Atmosphere on Grain Growth for CZTSe Absorbers Fabricated by Selenization of As-Sputtered Precursors

Formation of Alloyed Cu2Cox Zn1-x Sn(S,Se)4 Absorption Layer and Its Application in Solar Cells

Influence of H2Se Concentration on Se-rich CZTSSe Absorbers Sputtered with a Ceramic Quaternary Target

Controlling selenization equilibrium enables high-quality Cu2ZnSn(S, Se)4 absorbers for efficient solar cells

Achieving 11.95% Efficient Cu2ZnSnSe4 Solar Cells Fabricated by Sputtering a Cu-Zn-Sn-Se Quaternary Compound Target with a Selenization Process

High-sulfur Cu2ZnSn(S,Se)4 Films by Sulfurizing As-Deposited CZTSe Film: the Evolutions of Phase, Crystallinity and S/(S+Se) Ratio

Improving the Performance of Solution-Based CZTSSe Absorber by Selenization Annealing with Selenium Powder in Argon

Effect of Sn Content in a CuSnZn Metal Precursor on Formation of MoSe2 Film during Selenization in Se+SnSe Vapor

Influences of Cu Concentration on Electrical Properties of CZTSSe Absorbers and Their Device Performances

Segmented Control of Selenization Environment for High‐Quality Cu2ZnSn(S,Se)4 Films Toward Efficient Kesterite Solar Cells

Cu2ZnSnSSe4 Solar Cells with 9.6% Efficiency Via Selenizing Cu-Zn-Sn-S Precursor Sputtered from a Quaternary Target

Suppressing the formation of double‐layer in Cu 2 ZnSnSe 4 ( CZTSe ) absorber layer by facile heating process through nontoxic selenium atmosphere

The Effects of Selenium Content on Cu(Inga)Se-2 Thin Film Solar Cells by Sputtering from Quaternary Target with Se-Free Post Annealing

Using soda-lime glass transition temperature to enhance the efficiency of Cu2ZnSn(S,Se)4 solar cell

An Investigation on the Relationship Between Open Circuit Voltage and Grain Size for CZTSSe Thin Film Solar Cells Fabricated by Selenization of Sputtered Precursors

Influences Of The Selenization Duration On Compositions And Microstructures Of Cigs Absorber

Influences of Sulfurization on Performances of Cu(In,Ga)(Se,S)2 Cells Fabricated Based on the Method of Sputtering CIGSe Quaternary Target

Probing the effect of selenium substitution in kesterite-Cu2ZnSnS4 nanocrystals prepared by hot injection method