Abstract:A novel segmented control strategy for selenization environment is introduced to regulate the selenization reaction by controlling the evaporation area of Se. This selenization method helps to promote element homogenization, optimize surface smoothness, and obtain a high‐crystalline‐quality absorber with low‐point defects. And the CZTSSe solar cell with a PCE of 13.77% is successfully achieved. High‐crystalline‐quality absorbers with fewer defects are crucial for further improvement of open‐circuit voltage (VOC) and efficiency of Cu2ZnSn(S,Se)4 (CZTSSe) solar cells. However, the preparation of high‐quality CZTSSe absorbers remains challenging due to the uncontrollability of the selenization reaction and the complexity of the required selenization environment for film growth. Herein, a novel segmented control strategy for the selenization environment, specifically targeting the evaporation area of Se, to regulate the selenization reactions and improve the absorber quality is proposed. The large evaporation area of Se in the initial stage of the selenization provides a great evaporation and diffusion flux for Se, which facilitates rapid phase transition reactions and enables the attainment of a single‐layer thin film. The reduced evaporation area of Se in the later stage creates a soft‐selenization environment for grain growth, effectively suppressing the loss of Sn and promoting element homogenization. Consequently, the mitigation of Sn‐related deep‐level defects on the surface and in the bulk induced by element imbalance is simultaneously achieved. This leads to a significant improvement in nonradiative recombination suppression and carrier collection enhancement, thereby enhancing the VOC. As a result, the CZTSSe device delivers an impressive efficiency of 13.77% with a low VOC deficit.

Cu2ZnSnSSe4 Solar Cells with 9.6% Efficiency Via Selenizing Cu-Zn-Sn-S Precursor Sputtered from a Quaternary Target

Achieving 11.95% Efficient Cu2ZnSnSe4 Solar Cells Fabricated by Sputtering a Cu-Zn-Sn-Se Quaternary Compound Target with a Selenization Process

Cu2ZnSn(S, Se)4 solar cell with slight band tailing states achieves 11.83% efficiency by selenizing sputtered Cu–Zn–Sn–S precursor

CZTSSe solar cell with an efficiency of 10.19% based on absorbers with homogeneous composition and structure using a novel two-step annealing process

Improving the Performance of Solution-Based CZTSSe Absorber by Selenization Annealing with Selenium Powder in Argon

Above 10% efficient electrodeposited Cu2ZnSn(S,Se)4 solar cell achieved by modifying precursor

Efficient Cu2ZnSn(Se,S)4 solar cells with 79% fill factor using two-step annealing

Controlling selenization equilibrium enables high-quality Cu2ZnSn(S, Se)4 absorbers for efficient solar cells

Segmented Control of Selenization Environment for High‐Quality Cu2ZnSn(S,Se)4 Films Toward Efficient Kesterite Solar Cells

Preparing Cu2ZnSnSe4 thin film solar cells based on selenium containing precursors

10.24% Efficiency of Flexible Cu2 ZnSn(S,Se)4 Solar Cells by Pre-Evaporation Selenization Technique

An investigation on phase transition for as-sputtered Cu 2 ZnSnSe 4 absorbers during selenization

Influence of H2Se Concentration on Se-rich CZTSSe Absorbers Sputtered with a Ceramic Quaternary Target

Exploring the optimal two-step selenization process to enhance the performance of ionic liquid solution based Cu2ZnSn(S,Se)4 thin film solar cells

Unveiling the Selenization Reaction Mechanisms in Ambient Air-Processed Highly Efficient Kesterite Solar Cells

Uniform monolayer Cu2ZnSn(S,Se)4 film based on novel precursor solution

CZTSe solar cells prepared by electrodeposition of Cu/Sn/Zn stack layer followed by selenization at low Se pressure

Surprising Efficiency Enhancement of Cu 2 ZnSn(S,Se) 4 Solar Cells with Abnormal Zn/Sn Ratios

Effects of Selenium Atmosphere on Grain Growth for CZTSe Absorbers Fabricated by Selenization of As-Sputtered Precursors

Regulating Hetero‐Nucleation Enabling Over 14% Efficient Kesterite Solar Cells

Beyond 11% Efficient Cu2ZnSn(Se,S)(4) Thin Film Solar Cells by Cadmium Alloying