Abstract:The ability of wood–plastic composites (WPCs) to withstand various loads and resist plastic failure is attracting more and more interest due to the global increase in demand for WPCs by over 6 million tons per year. Among the most important and innovative research methods are those based on fracture mechanics—their results enable material designers to optimize the structures of these hybrid polymer composites at the nano, micro and macro levels, and they allow engineers to more accurately evaluate and select functional, sustainable, long-lasting and safe product designs. In this study, standard single-edge notched bending (SENB) tests were used to analyze the fracture toughness of two different extruded WPCs along the longitudinal (L) and transverse (T) directions of extrusion. In addition to their resistance to crack propagation, critical fracture criteria, initial contact stiffness, fracture parameters and fracture surfaces, the mechanical properties of these composites were also investigated. The results showed that WPC-A coded composites withstood higher loads until failure in both directions compared to WPC-B. Despite the larger data spread, both types of composites were more resistant to crack propagation in the T direction. Mode II of crack propagation was clearly visible, while mode III was not as pronounced. The experimental results and the numerical finite element (FE) model developed up to 58% of the maximum load correlated well, and the obtained deformation curves were best approximated using cubic equations (R2 > 0.99). The shear stress zone and its location, as well as the distribution of the equivalent stresses, had a major influence on crack propagation in the fracture process zone (FZP).

Correlation Between Fractal Dimension and Impact Strength for Wood Plastic Composites

Impact Strength and Fractal Characteristic of PLA-Based Wood Plastic Composites

Correlation Between Impact Strength and Fractal Dimensions of Fracture Surface for PLLA/nano-CaCO3 Composites

Crack Propagation And Fracture Process Zone (Fpz) Of Wood In The Longitudinal Direction Determined Using Digital Image Correlation (Dic) Technique

Understanding the Impact of Fibre Wrinkle Architectures on Composite Laminates Through Tailored Gaps and Overlaps

Relationship Between Fractal Dimensions of Fracture Surface and Impact Toughness of Polycaprolactone/nano‐caco3 Composites

Experimental and Numerical Investigation of the Fracture Behavior of Extruded Wood–Plastic Composites under Bending

Relationship Between the Fractal Dimension of Fracture Surface and the Impact Strength of ABS/HGB Composites

Low-velocity impact behavior and residual tensile strength of CFRP laminates

Study on Two-dimensional Fractal Characteristics of Fractography of Polypropylene/Diatomite Composites

Study on Relationship Between Impact Strength and Fracture Surface Fractal Dimension of PP/Nano-CaCO_3 Composites

Polylactide-Based Wood Plastic Composites Modified with Linear Low Density Polyethylene

Fractal characterization of impact fracture surface of polypropylene nanocomposites

Fracture-Surface Fractal Dimension of PP/Diatomite Composites and Its Relation to Impact Strength

Correlation between impact strength and fracture surface fractal dimension of ABS filled with hollow glass beads

Effect of wood flour and compatibilizer content on the properties of wood-plastic composites

Tensile Strength Of Wood Polylactic Acid Composite: A Meta-Analysis

Effect of Chemical Modification on Mechanical Properties of Wood-Plastic Composite Injection-Molded Parts

Recycling of waste FRP and corn straw in wood plastic composite

Study on Preparation and Properties of PLA/Wood Flour Composites

Study on flexural property of glass fiber-reinforced polymer reinforced wood–plastic composite panels