Abstract:Acrylonitrile-butadiene-styrene (ABS) terpolymer, unfilled and filled with calcium carbonate (calcite) particles, was used as a matrix for reinforcement with short glass fibers (SGF). All of the materials were prepared by injection molding and the fibers in the specimens were oriented preferentially in the flow direction (i.e. the axial direction of the specimens). The composites were studied with respect to the work of fracture (WOF), here the notched Charpy impact energy, determined by the Charpy V-notch impact test. The fracture surfaces of the composites were studied by scanning electron microscopy. The total WOF theory for short-fiber-reinforced composites was used to evaluate the interface energy and the matrix fracture work, whereby the fiber fracture work was neglected because of the brittleness of glass fibers, only a small amount of broken fibers being observed experimentally. It was shown that the interface energy is much higher than the matrix fracture work in the presence of fibers. The results showed that the reduction in WOF caused by adding SGF to pure ABS resin matrix is the consequence of a significant reduction in the matrix fracture work; on the other hand, the incorporation of SGF into calcite-filled ABS resulted to some extent in an increase in the WOF, this is being due to the relatively large interface energy contribution to the WOF of the composite. Moreover, it was observed experimentally that the treated case showed a higher WOF for SGF/ABS composites than for the as-received case, whereas this was not observed for hybrid SGF/calcite/ABS composites. This behavior was explained in terms of the changes in fiber length distribution by using the total WOF theory and the fiber pull-out energy theory. Furthermore, it was pointed out that when investigating the influence of the fiber/matrix interface on the WOF of short-fiber composites, the fiber length distribution must be taken into consideration.

Correlation between impact strength and fracture surface fractal dimension of ABS filled with hollow glass beads

Relationship Between the Fractal Dimension of Fracture Surface and the Impact Strength of ABS/HGB Composites

Mechanical Properties of Hollow Glass Bead-filled ABS Composites

Tensile and Flexural Properties of Hollow Glass Bead-filled ABS Composites

Fractal Quantitative Characterization of Disperse Effect of Glass Beads in Filled Polypropylene Composites

Impact fracture toughness of hollow glass bead-filled polypropylene composites

Grey Relationship Between Size Distribution of Hollow Glass Beads and Mechanical Properties of Filled Polypropylene Composites

Fracture Resistance of Unfilled and Calcite-Particle-filled ABS Composites Reinforced by Short Glass Fibers (SGF) under Impact Load

Effects of the Glass Bead Content and the Surface Treatment on the Mechanical Properties of Polypropylene Composites

Grey Relational Analysis between Size Distribution of Hollow Glass Beads and Impact Fracture Energy of Filled Polypropylene Composites

Fracture-Surface Fractal Dimension of PP/Diatomite Composites and Its Relation to Impact Strength

Correlation Between Impact Strength and Fractal Dimensions of Fracture Surface for PLLA/nano-CaCO3 Composites

Study on Two-dimensional Fractal Characteristics of Fractography of Polypropylene/Diatomite Composites

Tensile and impact properties of hollow glass bead-filled PVC composites

Fractal characterization of impact fracture surface of polypropylene nanocomposites

Effects of Filler Content and Size on Drop-Weight Dart Impact Fracture Behavior of Glass Bead-Filled Polypropylene Composites

Effect of Filler Content and Surface Treatment on the Tensile Properties of Glass-Bead-Filled Polypropylene Composites

Study on the Surface Properties of Colored Talc Filler (CTF) and Mechanical Performance of CTF/acrylonitrile-butadiene-styrene Composite

Effect of silica particle size and filler content on the fracture properties of epoxy resin composite

Gray Relational Analysis between Size Distribution and Impact Strength of Polypropylene/Hollow Glass Bead Composites

Study on Relationship Between Impact Strength and Fracture Surface Fractal Dimension of PP/Nano-CaCO_3 Composites