Abstract:The ability of wood–plastic composites (WPCs) to withstand various loads and resist plastic failure is attracting more and more interest due to the global increase in demand for WPCs by over 6 million tons per year. Among the most important and innovative research methods are those based on fracture mechanics—their results enable material designers to optimize the structures of these hybrid polymer composites at the nano, micro and macro levels, and they allow engineers to more accurately evaluate and select functional, sustainable, long-lasting and safe product designs. In this study, standard single-edge notched bending (SENB) tests were used to analyze the fracture toughness of two different extruded WPCs along the longitudinal (L) and transverse (T) directions of extrusion. In addition to their resistance to crack propagation, critical fracture criteria, initial contact stiffness, fracture parameters and fracture surfaces, the mechanical properties of these composites were also investigated. The results showed that WPC-A coded composites withstood higher loads until failure in both directions compared to WPC-B. Despite the larger data spread, both types of composites were more resistant to crack propagation in the T direction. Mode II of crack propagation was clearly visible, while mode III was not as pronounced. The experimental results and the numerical finite element (FE) model developed up to 58% of the maximum load correlated well, and the obtained deformation curves were best approximated using cubic equations (R2 > 0.99). The shear stress zone and its location, as well as the distribution of the equivalent stresses, had a major influence on crack propagation in the fracture process zone (FZP).
What problem does this paper attempt to address?
### Problems the Paper Attempts to Solve
This paper aims to investigate the fracture behavior of two different extruded wood-plastic composites (WPCs) under bending loads through experimental and numerical methods. Specifically, the research focuses on the following aspects:
1. **Fracture Toughness Analysis**: Analyze the fracture toughness of the two WPCs along the longitudinal (L direction) and transverse (T direction) directions through standard single-edge notched bend (SENB) tests.
2. **Crack Propagation Resistance**: Study the resistance of these composites to crack propagation, critical fracture criteria, initial contact stiffness, fracture parameters, and fracture surfaces.
3. **Mechanical Performance Evaluation**: In addition to fracture behavior, investigate other mechanical properties of these composites.
4. **Numerical Simulation**: Develop a finite element (FE) model to validate the experimental results and explore the stress distribution and deformation curves during the crack propagation process.
### Research Background
With the rapid global demand for wood-plastic composites (WPCs) (over 6 million tons annually), the study of their mechanical properties and fracture behavior has become particularly important. WPCs are widely recognized for their sustainability and long lifespan. However, information on the fracture behavior and crack propagation mechanisms of WPCs remains insufficient. Therefore, this study aims to fill this knowledge gap and provide scientific evidence for material design and engineering applications.
### Research Methods
1. **Sample Preparation**: Two types of extruded wood-plastic composite boards, WPC-A and WPC-B, were purchased from the market. WPC-A is made of recycled rigid unplasticized polyvinyl chloride (PVC-U) and Scots pine (Pinus sylvestris), while WPC-B is made of high-density polyethylene (HDPE) and moso bamboo (Phyllostachys edulis).
2. **Physical-Mechanical Performance Testing**: Physical-mechanical performance tests such as density, hardness, and strength were conducted in the laboratory.
3. **SENB Tests**: SENB tests were conducted according to ISO 13586:2018 and ASTM D5045-14 standards to evaluate the fracture toughness of WPCs in different directions.
4. **Numerical Simulation**: A numerical model was established using the finite element method (FEM) to validate the experimental results and further analyze the crack propagation process.
### Main Findings
1. **Fracture Toughness**: WPC-A exhibited higher fracture toughness in both directions, although the data was more dispersed.
2. **Crack Propagation Mode**: In the T direction, both WPCs showed stronger resistance to crack propagation. Crack propagation mainly exhibited mode II, while mode III was not significant.
3. **Numerical Simulation Results**: The experimental results were consistent with the predictions of the numerical model, with the deformation curve at 58% of the maximum load fitting best with a cubic equation (R² > 0.99).
4. **Crack Propagation Process**: The shear stress zone and its location, as well as the distribution of equivalent stress, significantly influenced the fracture process zone (FZP) during the crack propagation process.
### Conclusion
This study provides a detailed analysis of the fracture behavior of two different WPCs under bending loads through experimental and numerical methods, offering important scientific evidence for material design and engineering applications. The results indicate that WPC-A exhibits higher fracture toughness in both directions, with crack propagation mainly exhibiting mode II. The numerical simulation results are highly consistent with the experimental results, validating the effectiveness of the research methods.