Abstract:This study describes the laser surface hardening process effect on microstructures produced and their wear behavior. Ductile iron samples were austempered at three different austempering temperatures: 232 °C/288 °C/398 °C respectively. Then, the laser surface hardening process was applied on each sample. Different laser gaps were designed: 1.5mm/3mm/4 mm. The microstructures were observed using optical microscopy and tribo-tests were run using a UMT-3 tribo tester. A Rockwell hardness tester was used to measure the hardness after heat-treatment. Optical microscopy and SEM were used to observe the different microstructures and their distribution on the worn surface. The results showed that the laser processing generated ledeburite, martensite, or tempered bainite microstructures. Vickers hardness tests were carried out on these microstructures. The original needle-like microstructures were observed on the samples with 4 mm laser gap but not with 1.5 mm or 3 mm laser gap. This is because part of the 4 mm laser gap is beyond the laser heat effected zone. Generally, severe ploughing wear and smearing wear were observed on the tempered bainite zone but not the bainite zone. Debris was generated during the tribo-tests and led to three body abrasive wear which not only resulted in higher wear loss, but also polished the worn surface.

Wearability of Non-Smooth Surface with Laser Treatment in the Different Cooling Media

Wear Behavior of Die Steel with Non-smooth Surface in Different Shape and Distance

Wear Resistance of Die Casting Die of Cover Lid of Engine by Laser Treatment

Wear-Resistance of Die Steel with Non-Smooth Surface Used to Pressure Casting Die Processed by Laser

Friction and Wear Properties of Cast-iron Material with Bionic Non-smooth Surface under Normal Temperature

Investigation of Micro-wear and Micro-friction properties for bionic non-smooth concave components

Bio-inspired Wearable Characteristic Surface: Wear Behavior of Cast Iron with Biomimetic Units Processed by Laser

Friction and Wear Behavior Analysis of the Stainless Steel Surface Fabricated by Laser Texturing Underwater

Experimental Investigation on Anti-wear of ABionic Non-smooth Surface Made by LaserTexturing

Wear Behavior of Quenched Iron with Various Shapes and Unit Processed Through Two-Step Laser Alloying of C Powder

Investigation on Anti-Wear Ability of Bionic Nonsmooth Surfaces Made by Laser Texturing

Experimental Investigation On Anti-Wear Of A Bionic Non-Smooth Surface Made By Laser Texturing

Hardness Difference Effect of Biomimetic Surface with Hard-Soft Structure on Oil - Lubrication Wear Resistance

Experiment on Wear Resistance of 55 Steel Bionic Non-smoothed Surfaces at High Temperature

Sliding Wear Behavior of Laser Surface Hardened Austempered Ductile Iron

Study on laser prepared reinforcement unit distribution of large scale non-uniform hardness surface of gray cast iron against wear

Influence of processing medium on frictional wear properties of ball bearing steel prepared by laser surface melting coupled with bionic principles

The thermal fatigue resistance of cast iron with biomimetic non-smooth surface processed by laser with different parameters

Wear resistance of a bearing steel processed by laser surface remelting cooled by water

The Wear-Resistance of 3Cr2W8V Steel with Cave Pit Non-Smooth Surface Processed by Laser

Effects of Laser on the Non-Smooth Surface in Improving the Durability of Hot Forging Tools