Abstract:Joining alloys exhibiting individual superior properties could yield major benefits in terms of design and production flexibility. Nevertheless, differences in thermophysical properties between the materials to be joined complicate the formation of dissimilar combinations, thus limiting the potential applications of multiple engineering alloys. The formation of brittle Ti 2 Ni intermetallic (IMC) in the fusion zone (FZ) is the main challenge in joining NiTi to Ti6Al4V without an interlayer. Hence, the composition of the FZ needs to be changed to ideally suppress brittle IMC phases to form and decrease the likelihood of crack formation upon solidification. In this study, two strategies were used concurrently to reduce brittle Ti 2 Ni intermetallic compound: a cobalt interlayer was introduced in a butt joint configuration, and the laser was offset to the Ti6Al4V side. The use of a Co interlayer resulted in a joint free of brittle interaction layer susceptible to microcracks at the NiTi boundary by reducing the amount of brittle Ti 2 Ni intermetallic compound. A joint with a lower hardness of 438HV was attained, compared to 515HV for the conventional NiTi/Ti6Al4V joint. The maximum strength and fracture strain of the Co-interlayered joint were improved to 285MPa and 1.67%, respectively, compared to 148MPa and 0.8% for the Co-free joint.

Microstructure evolution and formation mechanism of laser-ignited SHS joining between C f /Al composites and TiAl alloys with Ni–Al–Ti interlayer

Microstructure and Formation Mechanism of SHS Joining Between C F /al Composites and TiAl Intermetallic with Al–Ni–CuO Interlayer

Effect of Ti–Al Content on Microstructure and Mechanical Properties of Cf/Al and TiAl Joint by Laser Ignited Self-Propagating High-Temperature Synthesis

High-efficiency Joining of Cf/Al Composites and TiAl Alloys under the Heat Effect of Laser-ignited Self-propagating High-temperature Synthesis

Formation Mechanism and Microstructure of C_f/Al and TiAl Joint by SHS Joining with Al-Ni-CuO Interlayer

Joining of Cf/Al Composites and TiAl Intermetallics by Laser-Induced Self-Propagating High-Temperature Synthesis Using the Ni-Al-Zr Interlayer

Joining of TiAl Intermetallic by Self-Propagating High-Temperature Synthesis

Effect of Reaction Heat on Reactive Joining of TiAl Intermetallics Using Ti–Al–C Interlayers

Mlicrostructure of TiAl/TiC cermet joint bonded by combustion synthesis

Microstructure of TiAl/TiC cermet joint bonded by combustion synthesis

Effects of Joining Conditions on Microstructure and Mechanical Properties of C F /al Composites and TiAl Alloy Combustion Synthesis Joints

Self-propagating Synthesis Joining of Cf/Al Composites and TC4 Alloy Using AgCu Filler with Ni–Al–Zr Interlayer

Combustion Joining of Carbon–carbon Composites to TiAl Intermetallics Using a Ti–Al–C Powder Composite Interlayer

Laser-induced Combustion Joining of Cf/Al Composites and TC4 Alloy

Microstructure, Macrosegregation, and Mechanical Properties of NiTi to Ti6Al4V Dissimilar Laser Welds Using Co Interlayer

Laser-Induced Exothermic Bonding of Carbon Fiber/Al Composites and Tial Alloys

SHS joining of TiAl intermetallics to TiB2 cermet

Active Brazing of C/C Composites and Single Crystal Ni-based Superalloy: Interfacial Microstructure and Formation Mechanism

Effect of Composition of Interlayer on TiAl/TiB2 Cermet Self-Propagating High-Temperature Synthesis Joint

Microstructure and mechanical properties of C f /SiC composite joints joined using AlCoCrFeNi 2.1 eutectic high-entropy alloy filler via spark plasma sintering

Microstructure and mechanical properties of Cf/Al-TiAl laser-assisted brazed joint