Abstract:Intermetallic alloys are synthesized in the 5Ti + 3Si + x Ni system by the method of self-propagating high-temperature synthesis (SHS) and mechanosynthesis. The influence of the nickel content on the morphology, size, and yield of composite particles after the mechanical activation (MA) of the mixtures is studied. The dependencies of the maximum temperatures and combustion rates, phase composition, morphology, and elongation of synthesis products on the nickel content for the initial and MA mixtures are studied. Under the conditions of the experiments conducted in this study, the combustion process is realized and at the same time the samples burn completely at a nickel content of 10 to 60 wt % in the 5Ti + 3Si + x Ni system. After the MA, the samples from the 5Ti + 3Si mixture burn completely, and during the activation of the 5Ti + 3Si + 40% Ni mixture, mechanochemical synthesis takes place. With the increasing nickel content, the combustion temperature decreases, and the combustion rate behaves nonmonotonically, the size of composite particles increases and the yield of the mixture after MA decreases. MA practically does not affect the maximum combustion temperatures of mixtures of 5Ti + 3Si + x Ni. A multiple (from 0.7 to 2.9 cm/s) increase in the burning rate of samples from MA mixtures with an increase in the Ni content from 20 to 30 wt % is recorded. An increase in the nickel content leads to an increase in the content of triple phases and the amount of melt in the synthesis products of mixtures of 5Ti + 3Si + x Ni.

Reaction Sintering and Joining Nickel Aluminide to AISI 316 Stainless Steel by Self-Propagating High Temperature Synthesis

Self-Propagating High Temperature Synthesis (SHS) of Intermetallic Compounds Titanium and Nickel Aluminides

Joining of TiAl Intermetallic by Self-Propagating High-Temperature Synthesis

Microstructure and Formation Mechanism of SHS Joining Between C F /al Composites and TiAl Intermetallic with Al–Ni–CuO Interlayer

Effect of Reaction Heat on Reactive Joining of TiAl Intermetallics Using Ti–Al–C Interlayers

The Effect of the Nickel Content and Mechanical Activation on Combustion in the 5Ti + 3Si + xNi System

High-efficiency Joining of Cf/Al Composites and TiAl Alloys under the Heat Effect of Laser-ignited Self-propagating High-temperature Synthesis

Microstructure evolution and formation mechanism of laser-ignited SHS joining between C f /Al composites and TiAl alloys with Ni–Al–Ti interlayer

Numerical investigation of sintering porous NiTi shape memory alloy by self-propagating high-temperature synthesis

Welding in Ti–Al and Ni–Al Systems by Self-Propagating High-Temperature Synthesis

Mathematical and experimental investigation of the self-propagating high-temperature synthesis (SHS) of TiAl3 and Ni3Al intermetallic compounds

Effect of self-propagating high-temperature combustion synthesis on the deposition of NiTi coating by cold spraying using mechanical alloying Ni/Ti powder

Preparation of NiAl-AlMg6 Functionally Graded Composite Using the Energy of a Highly Exothermic Ti-C Mixture during Self-Propagating High-Temperature Synthesis

Dissolution–precipitation mechanism of self-propagating high-temperature synthesis of mononickel aluminide

Preparation of Al–TiC Composites by Self-Propagating High-Temperature Synthesis

Effect of Al Content on Reaction Laser Sintering of Ni-Al Powder

Effect of a NiO Additive on Interaction in a Ni–Al–W System in Self-Propagating High-Temperature Synthesis

In Situ Synthesis of Al–TiC in Aluminum Melt

The efficiency assessment of Ni(40)Ti(50)Cu(x)Fe(10−x) shape memory alloy produced by combustion synthesis through thermal analysis

Fabrication and Joining of NiAl and TiAl Intermetallics by Additive Sintering

Self-propagating Synthesis Joining of Cf/Al Composites and TC4 Alloy Using AgCu Filler with Ni–Al–Zr Interlayer