Abstract:Molybdenum-silicon-boron (Mo-Si-B) alloy, which is considered a promising material for manufacturing aemengines, is mainly processed by methods including arc smelting and powder metallurgy. Selective laser melting (SLM), as the most commonly used processing method in additive manufacturing at present, provides another option for processing Mo-Si-B alloy. To study defects appearing during SLM of Mo-Si-B alloy, the effects of SLM parameters on the relative density were investigated based on orthogonal tests. It is found that the layer thickness has the largest influence on the relative density, followed by the laser power and hatch spacing, while the scanning speed exerts the smallest influence. By regulating SLM parameters, compact Mo-Si-B samples with a relative density larger than 99% can be obtained. Furthermore, a large number of intergranular cracks are found in Mo-Si-B alloy subjected to SLM, which can be regulated by preheating the substrate. When preheating the substrate at 400 degrees C, cracks on a horizontal section almost disappear and the reduction of cracks improves the compressive properties of the samples to some extent. The compressive strength of the samples without substrate preheating is 1065 MPa and it reaches 1610 MPa when preheating the substrate at 400 degrees C. The microhardness of the samples is about 360 HV, where the microhardness of a longitudinal section is higher than that of the horizontal section. Grains on each section have unique characteristics. For the longitudinal section, grains are columnar crystals along the building direction and the average grain size is about 8.69 mu m. In terms of the horizontal section, grains are irregular and the average grain size is 3.12 mu m. There are < 001 > textures in the main phases alpha-Mo of each section, and the existence of textures may lead to anisotropic properties of the samples.

Quantitative Analysis of Heterogeneous Microstructure and Diversified Strengthening Mechanisms in Spark Plasma Sintered Molybdenum Disilicide

Microstructure, Compressive Performance and Wear Resistance of Pure Molybdenum Additively Manufactured Via Laser Powder Bed Fusion

Influence of Spark Plasma Sintering Temperature on Sintering Behavior and Microstructures of Dense Bulk MoSi2

Effect of In-Situ Formed MoSi2 on Phase Transformation and Thermal Diffusivity of Spark Plasma Sintered Silicon Nitride

Effect of Mo Particle Size on Microstructure and Mechanical Properties of Spark Plasma Sintered Silicon Nitride

Microstructural Characterization of Sintered MoSi<sub>2</sub>/SiC<sub>P</sub> Composites

Processing of molybdenum disilicide

Regulation of Microstructures and Properties of Molybdenum‑silicon‑boron Alloy Subjected to Selective Laser Melting

Microstructural characterization of sintered MoSi2/SiCp composites

Effect of Temperature on the Microstructures of In-Situ MoSi_2 Fabricated by Spark Plasma Sintering

Microstructures and mechanical properties of reactive spark plasma-sintered ZrB2–SiC–MoSi2 composites

Microstructure and mechanical properties of SiC–mullite nanocomposite prepared by spark plasma sintering

The Microstructure and Cracking Behaviors of Pure Molybdenum Fabricated by Selective Laser Melting

Preparation and Mechanical Properties of Laminated Zirconium Diboride/molybdenum Composites Sintered by Spark Plasma Sintering

In Situ Synthesis of (Mo,Cr)Si2 Composites by Spark Plasma Sintering

Production of silicon carbide reinforced molybdenum disilicide composites using high-pressure sintering

Microstructure Evolution and Wear Properties of Bulk MoSi2 Fabricated by Field Activated Sintering

Influence of characteristic parameters of SiC reinforcements on mechanical properties of AlSi10Mg matrix composites by powder metallurgy

Microstructure and mechanical properties of a Mo-toughened Mo 3 Si-based in situ nanocomposite

A high entropy silicide by reactive spark plasma sintering

Microstructure Defects of MoSi2-SiC Composite Synthesized in Situ