Abstract:In the present work, effects of ZrC addition (10, 15, 20, 25 vol%) on microstructure and mechanical properties of ZTA20mol% (Zirconia-20mol% Toughened Alumina) ceramic composites were investigated. Samples were prepared by Hot Pressing Sintering (HP) at 1 600 ℃ and 30 MPa for a soaking time of 2 hours. Microstructures were characterized by XRD, Raman, SEM and TEM. XRD and Raman spectra results revealed that only ZrC, α-Al2O3 and ZrO2 were detected for all composites, indicating that these ceramic composites had excellent chemical compatibilities. SEM images showed refined microstructure was obtained, and the fracture surfaces exhibited a mixed process of transgranular and intergranular fracture. According to the TEM observations, some nano-sized ZrC particles dispersed inside Al2O3 grains and formed an intra/inter-type nanostructure. The relative densities and Vickers hardness were inversely proportional to ZrC content, which gradually decreased from 98.24% to 94.89%, from 1 847 to 1 691 HV1, respectively. Flexural strength and fracture toughness were tested by three-point bending method and single-edge notched beam method, respectively. The fracture toughness increased at first and then decreased with ZrC content increased from 0 to 25 vol%. The maximum value was 11.23 MPa.m1/2 with 20 vol% ZrC addition, with an enhancement of 51% compared to the undoped ZTA mixture. The flexural strength, with a maximum of 1 121 MPa without ZrC addition and decreased to 645MPa with ZrC-10(vol%) addition, then increased monotonously to 1084 MPa as the ZrC content increased from 10 to 25 vol%.

Mechanical Properties and Toughening Mechanism of WC-doped ZrB2–ZrSi2 Ceramic Composites by Hot Pressing

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Fabrication and mechanical properties of ZrB2–SiCw ceramic matrix composite

High-temperature deformation of ZrB2 ceramics with WC additive in four-point bending

Effects of SiC Platelet and ZrSi2 Additive on Sintering and Mechanical Properties of ZrB2-based Ceramics by Hot-Pressing

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Mechanical Properties of ZrB<sub>2</sub>-Based Ceramics Reinforced by Nano-SiC Whiskers

Preparation and characterization of high-toughness ZrB2/Mo composites by hot-pressing process

In Situ Preparation and Mechanical Properties of (ZrB2+ZrC)/Zr3[Al(Si)]4C6 Composites

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

Novel (Zr, Ti)B2-(Zr, Ti)C-SiC ceramics via reactive hot pressing

Preparation and Mechanical Properties of ZrB2-based Ceramics Using MoSi2 As Sintering Aids

Study on Mechanical Properties of Hot Pressing Sintered Mullite-Zro2 Composites with Finite Element Method

Microstructures and mechanical properties of B4C‐SiC and B4C‐SiC‐TiB2 ceramic composites fabricated by hot pressing

Synergistic strengthening and toughening of oscillatory pressure sintered WC-ZrO2-Al2O3 ceramics

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites

Microstructure And Mechanical Properties Of Zrb2-Based Composites With Laminated Structure

Chemical Process and Solid Solution Formation in Reactive Hot Pressed ZrB2–SiC Ceramics Doped with W

Microstructure, Mechanical, and Thermal Properties of in Situ-Synthesized (zrb2+sic)/zr2[al(si)]4c5 Composites

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride