Chemical Process and Solid Solution Formation in Reactive Hot Pressed ZrB2–SiC Ceramics Doped with W

H. -L. Liu,H. -B. Ma,J. -X. Liu,H. -T. Liu,G. -J. Zhang

DOI: https://doi.org/10.1080/17436753.2016.1257256

2016-01-01

Abstract:ZrB2-SiC doped with W was prepared from a mixture of Zr, Si, B4C and W via reactive hot pressing. The fully dense ZrB2-SiC-WB-ZrC ceramic was obtained at 1900 degrees C for 60 min under 30MPa in an argon atmosphere. Reaction path and solid solution characteristics of the starting powders were studied through a series of pressureless heat treatment at temperatures between 700 and 1500 degrees C. The solid solution phases of (Zr, W)B-2, (W, Zr)B and (Zr, W)C were formed directly by reactions between the precursors. Homogeneous distribution of solute atoms in solution and the solid solubilities were also studied.