Abstract:We reported the ferromagnetism (FM) and electrical transport properties induced by donor-acceptor compensated defect complexes and related impurity bands in highly compensated Zn-doped SnO 2 thin films. Various characterizations were used to study the optical, electrical, luminescent, and magnetic properties of SnO 2 films with Zn dopants. Comparing with the paramagnetic nature of undoped n-type SnO 2 , we observed a room temperature d 0 FM in the highly compensated and p-type Zn-doped SnO 2 films with a low conductivity of ∼10 −3 Scm −1 , suggesting a strong correlation between ferromagnetism and the donor-acceptor compensation. The coercive field, remanent and saturation magnetization for the Zn-doped SnO 2 film at 300 K are 310 Oe, 0.8 emu/cm 3 , and 2.6 emu/cm 3 , respectively. A detailed analysis for temperature-dependent resistivity indicates that the electrical conduction behavior of Zn-doped SnO 2 at low temperatures follows the variable range hopping mechanism proposed by Mott and confirms that impurity bands occur at the Fermi level. As the concentration of Zn dopants increases, the fitting Mott temperature gradually rises, suggesting the contribution of Zn impurities to form the impurity bands where the carriers are localized. First-principles calculations reveal that the Zn substituting Sn site (Zn Sn ) defect with a low formation energy is responsible for the transformation of the charge carrier type. Furthermore, the oxygen vacancy (V O ) between two nearest-neighbor Zn Sn defects can stabilize the ferromagnetic coupling and form Mott's variable range hopping conduction derived from the localized carriers in the compensated impurity bands. Our results are of significance for the better understanding of the physical mechanisms underlying the effects of impurity/defect bands on the magnetic and electrical properties of the SnO 2 with Zn dopants.

Unexpected ferromagnetism in n-type polycrystalline K-doped ZnO films prepared by RF-magnetron sputtering

Effect of Defects on Room-Temperature Ferromagnetism in Co and Na Co-Doped ZnO

Zn vacancy induced ferromagnetism in K doped ZnO

Room-Temperature Ferromagnetism in Epitaxial P-Type K-Doped Zno Films

Defect-induced Magnetism in Undoped Wide Band Gap Oxides: Zinc Vacancies in ZnO As an Example

Ferromagnetism Induced by Donor-Related Defects in Co-doped ZnO Thin Films

Influences of the Type of Dopant and Substrate on Ferromagnetism in ZnO:Mn

Oxygen Vacancy-Induced Ferromagnetism In Un-Doped Zno Thin Films

Intrinsic Ferromagnetism in Sm Doped Zno

Room-temperature ferromagnetism in p-type (Mn, N)-codoped ZnO thin films achieved by thermal oxidation of sputtered Zn<sub>3</sub>N<sub>2</sub>:Mn films

Room-temperature Ferromagnetism in Un-Doped ZrO2 Thin Films

Zn Vacancy Induced Room-Temperature Ferromagnetism in Mn-Doped Zno

Impurity-related defect complexes-mediated ferromagnetism and impurity band hopping conduction in a highly compensated Zn-doped SnO 2

Oxygen Enhanced Ferromagnetism in Cr-doped ZnO Films

Tunable Ferromagnetic Behaviors Observed in Highly Orientated Co‐Doped ZnO Thin Films by the Bandgap Engineering

Defect-induced Ferromagnetism in Insulating Mn–P Codoped ZnO Grown in Oxygen-Rich Environment

Donor Defects Enhanced Ferromagnetism in Co:Zno Films

Evidence of structural defect enhanced room-temperature ferromagnetism in Co-doped ZnO.

Room-temperature Ferromagnetism in Mn-N Co-doped P-Zno Epilayers by Metal-Organic Chemical Vapor Deposition

Magnetism of Co-Doped Zno Epitaxially Grown on A Zno Substrate

Substrate Effect on the Room-Temperature Ferromagnetism in Un-Doped ZnO Films