Abstract:In this study, highly c-axis-oriented ZnO:TM (TM = Co, Fe, and Mn) thin films doped with different doping levels (x = 0–10 at%) of TM were grown by chemical (sol-gel) and physical (magnetron sputtering) film deposition methods. These films were scrutinized by XRD, AFM, FESEM, EDX, XPS, Uv-Vis spectrophotometer, and VSM magnetometer. All the films have a powerful preferential c-axis orientation with a hexagonal polycrystalline structure. Comparatively, the stronger c-axis orientation and higher crystalline quality were observed for the chemically fabricated films than those physically derived. The chemically derived films had relatively higher roughness and it was decreased with increasing TM doping concentration. Compared to the ZnO, an increment in the crystallinity of chemically derived films was observed with an enhanced TM doping ratio, whereas a decrement in physically derived films was observed. The existence of Zn, Mn, Co, Fe, and O atoms and Zn 2+ , Co 2+ , Mn 2+ , and Fe 2+ ions were determined. Optical analysis revealed that the transmittance of chemically derived ZnO:TM thin films was relatively higher than physically produced, and the optical band gap of the films produced by both techniques was in good agreement with each other except for the ZMO. Magnetic measurements showed a clear room temperature ferromagnetic behavior for the ZnO:Mn and ZnO:Fe films. In contrast, paramagnetic behavior was observed for the chemically and physically produced ZnO:Co films. Among all films, the highest ferromagnetic response was obtained for the ZnO:Fe films due to their high crystallinity and purity. These outcomes reflect the produced films have great potential to be promising materials for optoelectronic and spintronic applications.

Tunable Ferromagnetic Behaviors Observed in Highly Orientated Co‐Doped ZnO Thin Films by the Bandgap Engineering

Evidence Of The Defect-Induced Ferromagnetism In Na And Co Codoped Zno

Effect of Defects on Room-Temperature Ferromagnetism in Co and Na Co-Doped ZnO

Ferromagnetic and Optical Behaviors Observed in Mn-Doped Zno-Based Thin Films

Defect-induced Magnetism in Undoped Wide Band Gap Oxides: Zinc Vacancies in ZnO As an Example

High-Tc ferromagnetism in a Co-doped ZnO system dominated by the formation of a zinc-blende type Co-rich ZnCoO phase.

Co–Ga Codoping Effect on Preferred Growth Orientations and Properties of Ferromagnetic ZnO Thin Films

Room-temperature ferromagnetic and ferroelectric behavior in polycrystalline ZnO-based thin films

Tunable Magnetic and Transport Properties of Single Crystalline (co, Ga)-codoped ZnO Films

Ferromagnetism Induced by Donor-Related Defects in Co-doped ZnO Thin Films

Ferromagnetic Behavior and Magneto-Optical Properties of Semiconducting Co-Doped ZnO

Grain boundary defects-mediated room temperature ferromagnetism in Co-doped ZnO film

Growth Technique–Induced Highly C-Axis-Oriented ZnO: Mn, Zno: Fe and ZnO: Co Thin Films: A Comparison of Nanostructure, Surface Morphology, Optical Band Gap, and Room Temperature Ferromagnetism

Evidence of structural defect enhanced room-temperature ferromagnetism in Co-doped ZnO.

Ferromagnetism Induced by Defect Complex in Co-doped ZnO

Magnetism of Co-Doped Zno Epitaxially Grown on A Zno Substrate

Fabrication and magnetic properties of co-doped ZnO thin films by pulsed laser deposition

Room temperature magneto-optics of ferromagnetic transition-metal doped ZnO thin films

Substrate-Dependent Magnetization In Co-Doped Zno Insulating Films

Optimizing physical properties of Co-doped ZnO nanoparticles: Controlling oxygen vacancy and carrier concentration

Ferromagnetic Enhancement and Magnetic Anisotropy in Nonpolar-Oriented (mn, Na)-Codoped Zno Thin Films