Phase Transition, Microstructure and Microwave Dielectric Properties of Α-Casio3 Ceramics with SiO2 Addition

Wei Hu,Hanxing Liu,Hua Hao,Zhonghua Yao,Minghe Cao,Zhijian Wang,Zhe Song,Haobo He

DOI: https://doi.org/10.1007/s10854-014-2637-0

2014-01-01

Journal of Materials Science Materials in Electronics

Abstract:The effect of SiO2 addition on phase transition, microstructure and microwave dielectric properties of α-CaSiO3 ceramics was reported for the first time. The X-ray diffraction analysis confirmed that the phase transformation from cyclo-CaSiO3 to pseudo-CaSiO3 was inhibited with the increase of SiO2 content. It was observed that the average grain size decreased with the increasing addition of SiO2 by scanning electron microscope. The τ f of the SiO2-added α-CaSiO3 ceramics almost remained constant with the SiO2 content increased, while the ε r and Q × f changed obviously. The optimized properties were determined for SiO2 6 wt% additive α-CaSiO3 ceramics sintered at 1,350 °C: ε r  = 7.37, Q × f = 33,714 GHz and τ f  = −11.08 ppm/°C.