Compositional Phases and Microwave Dielectric Properties of (Mg_(1-X)ca_x)_2al_4si_5o_(18) Ceramics

Liang Zheng
2012-01-01
Abstract:(Mg1-x,Cax)2Al4Si5O18 ceramics were fabricated by a conventional ceramic sintering method.The results by X-ray diffrac-tion showed that the(Mg,Ca)2Al4Si5O18 solid solution were formed in the range of 0≤x0.2,and(Ca,Mg)Al2Si2O8 solid solution was formed in the range of 0.8≤x≤1.0,and the composite phases of both Mg2Al4Si5O18 and CaAl2Si2O8 ceramics existed in the range of 0.2≤x0.8.The results by scanning electron microscopy showed that the porosity and micro-cracks of cordierite ceramics were effectively suppressed,the crystal growth and particle distribution of the composite phase of Mg2Al4Si5O18/CaAl2Si2O8 ceramics were controlled,along with Ca2+ doping.The dielectric constants of(Mg1-x,Cax)2Al4Si5O18 ceramics retained at 7.0 in the range of 0≤x≤0.4.Afterwards,it increased from 7.0 at x=0.6 to 8.6 at x=0.8 and then decreased to 6.9 at x=1.0.The Qf values decreased from 24 100 GHz of x=0 to 4 400 GHz of x=1.0 in the range of 0≤x≤1.However,the Qf value reached 5 500 GHz at x=0.6,due to the improvement of [Si,AlO4] inoic orders,which was higher than that of other compositional point in the range of 0.4≤x≤1.0.The temperature coefficients of resonant frequency(τf) of(Mg1-x,Cax)2Al4Si5O18 ceramics were -20×10-6 to -35×10-6 ℃-1.
What problem does this paper attempt to address?