Effect of Cobalt-Doping on the Dielectric Properties and Densification Temperature of Li2MgSiO4 Ceramic: Calculation and Experiment
Rui Peng,Yuanxun Li,Hua Su,Yongcheng Lu,Yanru Yun,Qin Zhang,Shijun Zhang
DOI: https://doi.org/10.1016/j.jallcom.2020.154162
IF: 6.2
2020-01-01
Journal of Alloys and Compounds
Abstract:The first principle calculation was conducted to predict the effect of Co2+ ion substitution on the crystal structure, electron density, formation energy and vibration properties of Li2MgSiO4 ceramic. All the samples were synthesised through the solid-state reaction method. Variations in sintering and dielectric properties were analysed through X-ray diffraction, scanning electron microscopy, network analysis, Raman spectrometry, thermomechanical analysis and simultaneous thermal analysis. Bond length, bond population and electron distribution in a MgO4 tetrahedron were modified due to the substitution of Mg2+ ion by Co2+ ion. The densification temperature was lowered from 1250 degrees C to 1050 degrees C with the addition of 5% (molar ratio) Co2+ ions. The sintering window was put forward slightly, and the vibration property was changed. The densification level and microwave dielectric properties were improved accordingly at following conditions: epsilon(r) = 5.75, Q x f = 26,500 GHz at 16 GHz, tau(f) = -9.4 ppm/degrees C and relative density = 95.2%. The dielectric and sintering properties of Li2MgSiO4 ceramic could be enhanced with the substitution of Mg2+ ion by Co2+ ion. (C) 2020 Elsevier B.V. All rights reserved.