Influence of Al 2 O 3 /SiO 2 ratio on the microstructure and properties of low temperature co-fired CaO–Al 2 O 3 –SiO 2 based ceramics

Zhenjun Qing,Bo Li,Hao Li,Yingxiang Li,Shuren Zhang

DOI: https://doi.org/10.1007/s10854-014-2150-5

2014-01-01

Abstract:In this work, in order to obtain the materials for low temperature co-fired ceramics applications, CaO–Al 2 O 3 –SiO 2 (CAS) based ceramics were synthesized at a low sintering temperature of 900 °C. The influences of Al 2 O 3 /SiO 2 ratio on the microstructure, mechanical, electrical and thermal properties were studied. According to the X-ray diffractomer and scanning electron microscopy results, the addition of the Al 2 O 3 is advantageous for the formation of the desired materials. Anorthite(CaAl 2 Si 2 O 8 ) is the major crystal phase of the ceramics, and the SiO 2 phase is identified as the secondary crystal phase. No new crystal phase appears in the ceramics with the increasing Al 2 O 3 content. More or less Al 2 O 3 addition would all worsen the sintering, mechanical and dielectric properties of CAS based ceramics. The ceramic specimen (Al 2 O 3 /SiO 2 = 20/18.5) sintered at 900 °C shows good properties: high bending strength = 145 MPa, low dielectric constant = 5.8, low dielectric loss = 1.3 × 10 −3 and low coefficient of thermal expansion value = 5.3 × 10 −6 K −1 . The results indicate that the prepared CAS based ceramic is one of the candidates for low temperature co-fired ceramic applications.