The Influence of Alumina to Microstructure and Dielectric Properties for Low Temperature Co-Fired Ceramics

Xuemin Cui,Ji Zhou,Jianhong Shen,Chunlin Miao

DOI: https://doi.org/10.3321/j.issn:1002-185X.2005.z2.060

2005-01-01

Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

Abstract:This paper studied the Ba-Ti-B-Si-O glass-ceramics composite, which was fabricated by calcined method with oxide solid at 750°C for LTCC. In general, the dielectric loss of glass ceramics that was fabricated directly by calcining was larger than pure ceramics material; hence good dielectric properties and microstructure were arrived by controlling the process parameter and additive in glass ceramics. The experimental results showed the mainly dielectric properties of LTCC materials were as following: ε ≈ 10, tan δ ≤ 2×10 -3 (1MHz). But the calcined method brought porous microstructure to LTCC, and it would result in instability of dielectric constant; hence, improved the microstructure of LTCC may get effective application. The research results showed the appropriate alumina additive of 2wt%-5wt% that could remove the pore in sintered body of LTCC, and the dielectric properties would worsen when the alumina additive exceeded 10wt%.