Microwave dielectric properties of (1 − x)(Mg 0.4 Zn 0.6 ) 2 SiO 4 –xCaTiO 3 composite ceramics

Wei Wang,Linjiang Tang,Wangfeng Bai,Bo Shen,Jiwei Zhai

DOI: https://doi.org/10.1007/s10854-014-2062-4

2014-01-01

Abstract:Phase formation, microstructure and microwave dielectric properties of (1 − x)(Mg 0.4 Zn 0.6 ) 2 SiO 4 –xCaTiO 3 (MZS-C) composite ceramics synthesized by using the conventional solid-state method were systematically investigated. Three phase structure was observed in all samples by using X-ray diffraction and the back scattering electron images. Mg 2 SiO 4 can form a solid solution with Zn 2 SiO 4 , which improved sinterability of the MZS-C composite ceramics. As the CaTiO 3 content was increased from 0.06 to 0.14, dielectric constant ε r and temperature coefficient of resonant frequency τ f values of the MZS-C ceramics sintered at 1,180 °C for 4 h increased from 6.74 to 8.35 and −41.5 to −6.46 ppm/°C, respectively. Zero τ f value can be obtained by properly adjusting the x value of the (1 − x)MZS–xC ceramics. With increasing content of CaTiO 3 , densification temperatures of the composite ceramics were decreased. The composite ceramic with x = 0.14 sintered at 1,180 °C for 4 h exhibited excellent microwave dielectric properties of ε r = 8.35, Q × f = 28,125 GHz and τ f = −6.46 ppm/°C.