Microwave Dielectric Properties and Thermally Stimulated Depolarization Currents of (1 − X)mgtio3–xca0.8sr0.2tio3 Ceramics

Jie Zhang,Zhenxing Yue,Yuanyuan Zhou,Xiaohua Zhang,Longtu Li

DOI: https://doi.org/10.1111/jace.13485

IF: 4.186

2015-01-01

Journal of the American Ceramic Society

Abstract:(1 − x)MgTiO3–xCa0.8Sr0.2TiO3 (0.04 ≤ x ≤ 0.2, MT‐CST) composite ceramics were prepared by the conventional solid‐state reaction process. The phase composition, microwave dielectric properties, and microwave dielectric loss mechanisms were studied. Ca0.8Sr0.2TiO3 was employed as a τf compensator for MgTiO3, and they coexisted well without forming any secondary phases. Interestingly, significant dielectric relaxations associated with oxygen vacancy defects were observed in all the MT‐CST ceramics through the dielectric‐temperature spectra. Thermally simulated depolarization current was therefore conducted to obtain the defects associated with extrinsic dielectric loss mechanisms. The concentrations of both defect dipole and in‐grain oxygen vacancies increased with the increasing x, which could induce microwave dielectric loss consequently. It demonstrated that the behaviors of Q × f were basically influenced by phase composition and defects here. Temperature‐stable ceramics can be achieved at x = 0.06, where the microwave dielectric properties were εr = 21.19, Q × f = 110 900 GHz (f = 9.295 GHz), and τf = −0.9 ppm/°C, respectively.