Low-loss (1-X)ba0.6sr0.4la4ti4o1 5-Xcatio3 Microwave Dielectric Ceramics with Medium Permittivity

Xiaohua Zhang,Ning Chang,Jie Zhang,Yuanyuan Zhou,Zhenxing Yue,Longtu Li

DOI: https://doi.org/10.1016/j.jallcom.2019.153011

IF: 6.2

2020-01-01

Journal of Alloys and Compounds

Abstract:In the present work, a series of (1-x)Ba0.6Sr0.4La4Ti4O15-xCaTiO(3) (x = 0.02, 0.03, 0.05, 0.1 and 0.2, BSLT-CT) functional ceramics were synthesized via co-firing the mixtures of Ba0.6Sr0.4La4Ti4O15 and CaTiO3 powders. Crystal structure and microwave dielectric properties were investigated together thermally stimulated depolarization currents (TSDC). Scanning electron microscopy (SEM) would be explored. X-ray diffraction confirms that these compounds display a single hexagonal phase with perovskite structure and the diffraction peaks shift to high angles with increasing CaTiO3 content. Raman spectra uncover O-h symmetry deviation and distortions of oxygen octahedra. The variation of the CaTiO3 addition has a direct impact on the dielectric properties of the (1-x)BSLT-xCT ceramics at microwave frequency. TSDC was conducted to acquire the defects associated with extrinsic microwave loss mechanism. The main type of defect in BSLT-CT is oxygen vacancy (V-o(center dot center dot)), namely involving in-grain and across-grain relaxation. The increase of CaTiO3 prompts the increase of oxygen vacancy concentration, which may induce microwave loss. At x = 0.2, the microwave dielectric properties of specimens are epsilon(r) = 47.1, Q x f = 41,200 GHz and tau(f).= -5.3 ppm/degrees C, respectively. (C) 2019 Elsevier B.V. All rights reserved.