Effect of TiO 2 on microstructure and microwave dielectric properties of TiO 2 –CaF 2 ceramics prepared by two-step sintering assisted by cold sintering
Ningjie Guo,Shenfeng Long,Guisheng Zhu,Huarui Xu,Xupeng Jiang,Xiuyun Zhang,Jinjie Song,Tingting Wei,Yunyun Zhao,Kunpeng Jiang,Yaoben Xu,Dabin Liang,Tianying Huang
DOI: https://doi.org/10.1007/s10854-023-11150-x
2023-01-01
Abstract:CaF 2 with low ε r has excellent microwave dielectric properties, Q f = 26,448 GHz, ε r = 6.48, τf = − 106 ppm/°C. However, its relatively negative temperature coefficient of resonant frequency ( τf ) greatly inhibits its commercial application. In this work, x TiO 2 –CaF 2 ( x = 0 wt%, 0.05 wt%, 0.1 wt%, 0.125 wt%, 0.15 wt%) ceramics were prepared by cold-sintering assisted two-step sintering method, and the effects of TiO 2 addition amount on phase composition, microstructure and microwave dielectric properties were systematically studied. It was found that 0 wt% TiO 2 –CaF 2 (the pure CaF 2 ) ceramics obtained a high Q f value of 66,043.27 GHz after two steps of cold-sintering-assisted sintering, which was 2.5 times higher than that of conventional sintering (Q f = 26,448 GHz). X-ray diffraction and scanning electron microscopy (SEM) data show that the added TiO 2 reacts with CaF 2 matrix to generate CaTiO 3 during high-temperature sintering. In addition, with the increase of x , ceramic τf is gradual increase, while ε r and Q f decrease to a certain extent. The optimal microwave dielectric property combination with τ f value near zero (Q f = 14,080.74 GHz, ε r = 6.87, τf = − 3.79 ppm/°C) was obtained at x = 0.1 wt% and 950 °C. The good chemical compatibility between TiO 2 –CaF 2 ceramics and Ag is verified, which indicates that they have broad application prospects in low temperature cofired ceramic technology.