Abstract:In this study, a novel technique of consecutive multi-pass cooperative lowered-temperature rolling (CMCLR) was proposed for the first time, with the purpose of preparing high performance wrought magnesium alloys. Based on this, a highly ductile magnesium alloy sheet could be effectively produced from ingot. The corresponding microstructure could directly evolve from coarse dendrites to equiaxed grains with an average size of similar to 5 mu m, which was attributed to the intense dynamic recrystallization (DRX) during isothermal deformation. The equivalent strain gradually decreased from the surface to the interior and edge of the rolled sheet due to the anisotropic plastic deformation. Instead, the temperature of the core of the sheet was slightly higher than that of the surface due to the deformation heat effect. The basal texture in the RD-TD plane generally weakened in the form of the splitting of basal texture toward the RD and the broadening of basal plane away from the pole center due to texture randomization dominated by DRXed grains. The exceptional ductility of more than 28.7% together with acceptable ultimate tensile strength of not less than 267 MPa was ascribed to the progressive work hardening as a result of seamless switching of multiple deformation modes, i.e., basal dislocation-slip-mediated deformation was preferentially operated and then was substituted by twinning-controlled deformation and non-basal dislocation-slip-dominated deformation. The selection of {10 (1) over bar2} twin variants agreed well with geometrical compatibility factor (m') criterion instead of Schmid's law. The activated twin variants nearly engulfed the whole parent grains for the sake of preserving compatible deformation continuity at ambient temperature, giving rise to the formation of TD-split texture. Comparatively, the {10 (1) over bar2} twinning could randomize the basal texture via reorienting grain orientations which in turn facilitated the reactivation of dislocation slip systems in the case of high temperature deformation.

Textural Evolution of AZ31B Magnesium Alloy Sheets Undergoing Repeated Unidirectional Bending at Room Temperature

Dramatically enhanced stamping formability of Mg–3Al–1Zn alloy by weakening (0001) basal texture

Enhancement of Tensile Ductility and Stretch Formability of AZ31 Magnesium Alloy Sheet Processed by Cross-Wavy Bending

Mechanical Properties and Texture Evolution During Rolling Process of an AZ31 Mg Alloy

Mechanical Anisotropy and Deep Drawing Behaviors of Az31 Magnesium Alloy Sheets Produced by Unidirectional and Cross Rolling

Effect of Stretch Bending on the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

Microstructure Evolution and Mechanical Behavior of AZ31 Magnesium Alloy Sheet with Bimodal Texture under Bending Deformation

Effect of texture types on microstructure evolution and mechanical properties of AZ31 magnesium alloy undergoing uniaxial tension deformation at room temperature

Formability Improvement for Bending Magnesium Alloy AZ31 Sheet via Microstructural Control

Effect of Initial Texture on the Bending Behavior, Microstructure and Texture Evolution of ZK60 Magnesium Alloy During the Bending Process

Texture Evolution of AZ31 Magnesium Alloy Sheets During Warm Rolling

Mechanical properties and texture evolution during hot rolling of AZ31 magnesium alloy

Texture modification and mechanical properties of AZ31 magnesium alloy sheet subjected to equal channel angular bending

Microstructure Evolution and Mechanical Properties of Az91d Magnesium Alloy Processed by Repetitive Upsetting

Enhanced Microstructure Homogeneity and Mechanical Properties of AZ31 Magnesium Alloy by Repetitive Upsetting

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Multiple-twinning induced recrystallization and texture optimization in a differential-temperature-rolled AZ31B magnesium alloy with excellent ductility

Effect of Final Rolling Temperature on Microstructures and Mechanical Properties of AZ31 Alloy Sheets Prepared by Equal Channel Angular Rolling and Continuous Bending

Microstructure Evolution of AZ31B Magnesium Alloy Sheets Deformed in Different Deformation Directions

An Exceptional Ductility of AZ31 Magnesium Alloy Sheet Achieved by Consecutive Multi-Pass Cooperative Lowered-Temperature Rolling

Microstructure Evolution and Mechanical Properties of AZ31 Alloy with Accumulative Roll Bonding