Abstract:In-plane uniaxial tension of AZ31 magnesium alloy sheet with non-basal texture has been conducted in order to demonstrate the effects of loading direction on the microstructure evolution and mechanical properties at ambient temperature. Loading axes are chosen to be along five directions distributed between rolling direction (RD) and transverse direction (TD), allowing various activities in involved slip and twinning modes to take place. As for twinning modes, electron backscattered diffraction observations confirm that the contribution of \({{\{ 10\overline{1}1\} }}\) compression twinning is minimal to the plastic deformation of all deformed samples. By comparison, \({{\{ 10\overline{1}2\} }}\) extension twinning (ET) not only serves as an important carrier on sustaining and accommodating plastic strain but also contributes to the emergence of TD-component texture with the progression of plastic strain. In terms of slip modes, analysis on Schmid factor demonstrates that the increasing tilted angle between loading direction and RD of sheet is unfavorable to the activation of basal <a> slip, whereas it contributes to the activation of prismatic <a> slip. These observations consequently explain the increasing tendency of 0.2% proof yield stress. Moreover, the activations of basal <a> slip and \({{\{ 10\overline{1}2\} }}\) ET collectively contribute to the concentration of two tilted basal poles toward normal direction. With increasing angle between loading direction and RD, the activations of basal <a> slip and \({{\{ 10\overline{1}2\} }}\) ET are gradually weakened. This leads to a weakening tendency about concentration of two tilted basal poles, a generally increasing tendency about Lankford value (r-value) and a generally decreasing tendency about strain-hardening exponent (n-value).

Microstructure Evolution of AZ31B Magnesium Alloy Sheets Deformed in Different Deformation Directions

Microstructure Evolution and Mechanical Behavior of AZ31 Magnesium Alloy Sheet with Bimodal Texture under Bending Deformation

Microtexture Evolution Via Deformation Twinning and Slip During Compression of Magnesium Alloy AZ31

Asymmetry in the hot deformation behavior of AZ31B magnesium sheets

Effect of texture types on microstructure evolution and mechanical properties of AZ31 magnesium alloy undergoing uniaxial tension deformation at room temperature

Microstructure and Texture Evolution of Az31 Magnesium Alloy During Large Strain Hot Rolling

Dependence of Microstructure Evolution and Mechanical Properties on Loading Direction for AZ31 Magnesium Alloy Sheet with Non-basal Texture During In-Plane Uniaxial Tension

Structure Evolution of Az31 Mg Alloy Sheet During Bidirectional Cyclic Bending at Low Temperature and Subsequent Annealing

Mechanical Properties and Microstructure Evolution of AZ31 Magnesium Alloy Sheet Subjected to High Strain Rates Loading of Different Orientations

Microstructure and Texture Evolution of AZ31 Magnesium Alloy During Rolling

Evolution of Microstructure and Texture During Uniaxial Compression of Cast AZ31Mg Alloy at Elevated Temperatures

Microstructure Evolution During High Strain Rate Tensile Deformation of A Fine-Grained Az91 Magnesium Alloy

Dynamic Recrystallization and Texture Development During Hot Deformation of Magnesium Alloy AZ31

Dynamic Recrystallization and Microstructure Evolution in AZ31 Magnesium Alloy During Thermomechanical Processing

Microstructure evolution and mechanical response of extruded AZ31B magnesium alloy sheet at large strains followed by annealing treatment

Experiment and Crystal Plasticity Analysis on Plastic Deformation of AZ31B Mg Alloy Sheet under Intermediate Temperatures: How Deformation Mechanisms Evolve

Microstructural Evolution of Az61 Magnesium Alloy During Hot Deformation

Microstructures and tensile properties of commercial AZ31B magnesium alloy sheets

Microstructure Evolution of AZ91D Magnesium Alloy During High Temperature Compression

Dynamic mechanical response and microstructural evolution of extruded Mg AZ31B plate over a wide range of strain rates

Research on Deformation Mechanism of AZ31 Magnesium Alloy Sheet with Non-Basal Texture During Uniaxial Tension at Room Temperature: A Visco-Plastic Self-Consistent Analysis