Abstract:In this study, {10-12} tensile twins (TTs) were induced in hot-rolled AZ31 Mg sheets via hot tension along the normal direction. The results demonstrate that the volume fraction of TTs at 2mm/min is greatly lower than their counterparts at 0.5mm/min at 100°C and 200°C. Dynamic recrystallization (DRX) can decrease twin nucleation rate during hot tensile when the strain rate reaches 2mm/min. Decrease in critical resolved shear stress of non-basal slips at 200°C enhances the deformation capability among grains, which dramatically reduces the volume fraction of TTs. Hence, TTs are hardly observed in 200°C-2mm/min sample. Tensile temperature significantly affects the morphology of TT lamellae. Grain boundaries prevents the longitudinal growth of the TTs, and then the thickness of TTs begins to grow to coordinate the deformation, resulting in fine TT lamellae in 100°C-0.5mm/min. Compared with AR, the basal texture intensity of 100°C-2mm/min and 200°C-2mm/min increases and the occurrence of DRX is the main reason, while basal texture weakening of 100°C-0.5mm/min and 200°C-0.5mm/min depends on the formation of TTs. Compared with samples at 200°C, the samples at 100°C have higher tensile stresses. The maximum stress of 100°C-0.5mm/min is 64.97 MPa when tensile strain reaches 0.15 owing to its highest dislocation density. 200°C-2mm/min possesses the highest hardness among the four tension samples, which is associated with the largest fraction of DRXed grains (68.8%) and its refinement strengthening effect. Dislocation strengthening exerts more influence on the hardness of 100°C-0.5mm/min.

Microstructure Evolution of AZ91D Magnesium Alloy During High Temperature Compression

Microtexture Evolution Via Deformation Twinning and Slip During Compression of Magnesium Alloy AZ31

Hot Deformation Behavior and Microstructural Evolution of Twin-Roll-Casting Mg Alloy during High-Temperature Compression

Microstructure of semi-solid AZ91D magnesium alloy after hot compression

Microstructure evolution of AZ80 magnesium alloy in semi-solid compression by molecular dynamics simulation

Microstructure in as-cast AZ61 magnesium alloy during hot compression deformation

Microstructure evolution and characterization of the adiabatic shear bands in AZ31 magnesium alloy

Hot deformation behavior of AZ40 magnesium alloy at elevated temperatures

Deformation behavior and microstructure evolution of AZ31 Mg alloy during gradient thermal compression

High Temperature Deformation Behavior of Fine-Grained AZ31 Magnesium Alloy

Twinning Behavior, Microstructure Evolution and Mechanical Property of Random-Orientated ZK60 Mg Alloy Compressed at Room Temperature

A comprehensive analysis on microstructure evolution of Mg-5.65Zn-0.66Zr alloy during hot deformation

Evolution of microstructure and texture of AZ80 magnesium alloy under hot torsion with constant decreasing temperature rate

Mechanical properties and failure behavior of AZ61 magnesium alloy at high temperatures

Microstructural Characteristics and Subsequent Soften Mechanical Response in Transverse Direction of Wrought AZ31 with Elevated Compression Temperature

The high-temperature deformation and microstructural evolution mechanism of Mg-Gd-Y-Zn-Zr alloy formed by CMT arc additive forming

Effect of deformation conditions on twinning of AZ31 magnesium alloy during compression test

Nanocrystallization and precipitation behavior evolution of AZ80 magnesium alloy during multi-directional compression

Dynamic recrystallization and twinning behavior of magnesium alloy during hot tension

Microstructure Evolution and Mechanical Behavior of AZ31 Magnesium Alloy Sheet with Bimodal Texture under Bending Deformation

Unveiling the Microstructural Features during Compression of a High-Modulus Mg-15Gd-8Y-6Al-0.3Mn Alloy Reinforced by a Large Volume of Al2RE Phases