Microstructure of semi-solid AZ91D magnesium alloy after hot compression

Wenyuan Gong,Guijie Zhang,Xiaoping Zheng,Yaqiang Tian,Jinying Song,Liansheng Chen

DOI: https://doi.org/10.13251/j.issn.0254-6051.2017.08.008

2017-01-01

Abstract:At the 0.001~10 s-1 of strain rate and 300~400 ℃ of temperature, the high temperature compressive behavior of AZ91D magnesium alloy semi-solid billet prepared by rolling induced melting activation method was investigated by means of Gleeble-3500 thermal simulation test machine.Effects of strain rate and deformation temperature on microstructure of the samples were studied.The microstructure characteristics of each deformation zone were analyzed.Results show that the strain rate and deformation temperature are both important factors to affect the microstructure, the smaller the strain rate, the higher the deformation temperature, the larger the average size of the grain, the better the uniformity of the grain size.After hot compression, the α-Mg solid particles are compressed in the vertical direction, and the "liquid phase" is not obvious, which indicates that the α-Mg solid particles have a good plastic deformation capacity, while the "liquid phase" is poor.The microstructure characteristics of different deformation zones in the compression specimens show obviously different that the solid particles in the center are easily deformed, while these in the other parts are relatively hard;the "liquid phase" is squeezed to the two sides of the sample, while the solid phase has no obvious segregation which shows that the "liquid phase" moves more easily than the solid phase particles in the press working process.