High Temperature Deformation Behavior of Fine-Grained AZ31 Magnesium Alloy

胡燕辉,李建国,谭敦强,曹凑先

DOI: https://doi.org/10.3969/j.issn.1005-5053.2010.1.007

2010-01-01

Abstract:Unidirectional hot compressive tests of AZ31 magnesium alloy after grain refinement were performed by Gleeble-1500 machine at strain rates changed among 0.01~1s-1 and deformation temperature varied among 300~450℃.Each parameter of the constitutive equation was gained by analyzing and calculating the results of samples,and a complete constitutive equation of AZ31 magnesium alloy for high temperature was fabricated,furthermore,the microstructures of compressive samples were studied.The results show that the hot deformation activation energy Q is 177.181 kJ/mol and the stress exponent n is 6.24.Compared with the edge of the compressive samples,the center has more intense degeneration.With the temperature increasing,obvious recrystallization is observed in the compressive organization.The new grain forms toward the crystal boundary and then grows up.