New perspective on the texture evolution mechanism of Si3N4 ceramics: Effect of additive content
Yunwei Shi,Qianglong He,Aiyang Wang,Hao Wang,Weimin Wang,Zhengyi Fu
DOI: https://doi.org/10.1016/j.ceramint.2023.01.136
IF: 5.532
2023-03-01
Ceramics International
Abstract:The effect of additive content on the texture evolution of Si3N4 ceramics prepared by hot-pressing at 1750 °C was investigated. When the amount of additive was insufficient, the liquid converted some of the α-Si3N4 powder into a few elongated β-grains and numerous isometric β-grains during heating. Afterwards, the deficient residual liquid caused a few isometric β grains to be randomly elongated and coarsened, resulting in a strong texture degree of 0.126 f L during holding. As the additive content was moderately increased, the texture degree decreased to 0.108 owing to the formation of more randomly elongated grains, which significantly weakened the texture. Moreover, when the additive was abundant, the superfluous liquid phase facilitated the elongation and coarsening of all β grains, resulting in a strong texture of 0.213 f L . The IOP and MRD values demonstrated a similar tendency for the texture degree in Si3N4 ceramics. Therefore, the texture evolution mechanism provides a new understanding of more accurately regulating the texture microstructure in Si3N4 ceramics.
materials science, ceramics