Abstract:Si3N4 ceramic with ultrafine fibrous grains are expected to exhibit remarkable mechanical properties. In this work, highly porous Si3N4 ceramic monoliths composed of ultrafine fibrous grains were developed via a novel vapor-solid carbothermal reduction nitridation (V-S CRN) reaction between SiO vapor and green bodies comprised of carbon nanotubes (CNTs), α-Si3N4 diluents and Y2O3 in a N2 atmosphere. The unique fibrous grains-interconnected structure was developed through in-situ formation of Si3N4 and following liquid phase sintering. The porous Si3N4 monoliths with porosity of 61–78% was developed by controlling the contents of α-Si3N4 diluents and densities of the CNT green bodies. With increasing of the α-Si3N4 contents, Si3N4 fibrous grains with an aspect ratio of approximate or higher than 20 could be achieved, and the grains were gradually refined. For the samples with 40 wt% α-Si3N4, the minimum mean grain diameter and pore size of 164 nm and 0.79 μm were achieved, respectively, and the resultant porous Si3N4 monolith exhibited a flexural strength of as high as 73–102 MPa with the porosity of 61–73%, which is much higher than that of the reported in literature. The improvement of mechanical strength could be attributed to the densely interconnected bird's nests structure formed by the ultrafine fibrous grains. The effects of the α-Si3N4 diluents on the resulting porous Si3N4 monolith via this method were analyzed.

Effects of Β-Si3n4 Seeds Addition on Microstructure and Mechanical Properties of Porous Si3N4 Ceramics

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Effect of Sintering Additive Content on Mechanical and Dielectric Properties of Porous Si3N4/BN Composite Ceramics

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

Effects of MgSiN2 Addition and Post-Annealing on Mechanical and Thermal Properties of Si3N4 Ceramics

Effect of the Residual Phases in Β-Si3n4 Seed on the Mechanical Properties of Self-Reinforced Si3N4 Ceramics

Effects of seeds on the thermal conductivity of self-toughened Si3N4 ceramics

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

Influence of α-Si3N4 coarse powder on densification, microstructure, mechanical properties, and thermal behavior of silicon nitride ceramics

Effects of additives to Si3N4 matrix on microstructure and properties of laminated Si3N4/BN ceramics

Preparation And Properties Of High Strength Porous Si3n4 Ceramics

Preparation of β-Si3N4 Seeds and Self-reinforced Si3N4 Ceramics

Preparation and Properties of Micro porous Si3N4 Ceramics by Gelcasting

Fabrication and Characterization of β-Si3N4 Seeds with Additive of Lu2O3

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

Study Of The Comparative Effect Of Sintering Methods And Sintering Additives On The Microstructure And Performance Of Si3n4 Ceramic

Microstructure and Performance of Silicon Nitride Ceramics with Lu2O3 Additives

Preparation of Porous Si 3 N 4 Ceramics Via Tailoring Solid Loading of Si 3 N 4 Slurry and Si 3 N 4 Poly-Hollow Microsphere Content

Effects of Sintering Additives on Microstructure and Properties of Porous SiC Ceramics with High Porosity

Microstructure and Properties of Porous Si3n4 Ceramics with A Dense Surface