Abstract:In this paper, cordierite-based porous ceramics with magnetic properties have been firstly in-situ synthesized by using MgO, Al 2 O 3 , and SiO 2 powders as raw materials and Fe 3 O 4 as a functional additive. Combining with the foam freeze casting method, near net size fabrication (total linear shrinkage < 2.86%) of the magnetic porous materials was realized by adjusting the amount of Fe 3 O 4 . The porosity, compressive strength, and saturation magnetization of the prepared materials were 83.9%–87.8%, 1.51–2.65 MPa, and 1.2–5.8 emu/g, respectively. The phase composition and microstructure evolutions during sintering were investigated briefly. The results showed that the synthesis temperature of cordierite was lowered about 100 °C due to the addition of Fe 3 O 4 . Except for the main phase-cordierite, Mg—Al—Fe spinel and α-Fe 2 O 3 also existed in the final materials. The lattice parameters of the Mg—Al—Fe spinel and the amount of α-Fe 2 O 3 changed obviously with the change in the sintering temperature and Fe 3 O 4 amount, which mainly influenced the magnetic properties of the prepared materials. Thus, a facile fabrication method of the cordierite-based porous ceramics with the magnetic properties has been put forward in this paper.

Preparation of textured porous Al2O3 ceramics by slip casting in a strong magnetic field and its mechanical properties

Effect Of Beta-Si3n4 Initial Powder Size On Texture Development Of Porous Si3n4 Ceramics Prepared By Gel-Casting In A Magnetic Field

Preparation of C-Axis Textured SiC Ceramics by a Strong Magnetic Field of 6 T Assisted Gel-Casting Process

Fabrication of Textured Si3N4 Ceramics with Β-Si3n4 Powders As Raw Material by Gel-Casting under Strong Magnetic Field

Alumina Ceramic Texturing Induced by High Magnetic Field and Its Microstructure

Effect Of The Initial Time Of Polymerization On Texture Of Si3n4 Ceramics In A Strong Magnetic Field

Porous textured ceramics with controlled grain size and orientation

Control Of Ceramic Material Microstructure With Super High Magnetic Field

Effect of Seed Particles Content on Texture Formation of Si 3 N 4 Ceramics by Gel-Casting in a Strong Magnetic Field

Effect of Sintering Conditions on Texture Formation of Si3N4 Ceramic Shaped Up in a Strong Magnetic Field

Magnetic slip casting: a review of current achievements and issues

Preparation and anisotropic properties of textured structural ceramics: A review

Ultrafast high-temperature sintering of dense and textured alumina

Facile fabrication of cordierite-based porous ceramics with magnetic properties

Giant permittivity in (Nb0.5La0.5)xTi1‐xO2 ceramics prepared by slip casting in a strong magnetic field

Anisotropic Sintering Shrinkage And Grain Growth For Spherical Alumina Powder Compacts Aligned In High Magnetic Field

Fabrication of Porous Alumina Ceramics with Directional Pore Channels Structure by Freeze-Gel Casting Processing

Anisotropic properties of textured h-BN matrix ceramics prepared using 3Y2O3-5Al2O3(-4MgO) as sintering additives

Anisotropic Sintering Shrinkage of Spherical Alumina Particle Compact Aligned in High Magnetic Field

Porous Al2o3 Prepared Via Freeze Casting And Its Biocompatibility

FABRICATION OF POROSITY GRADIENT ALUMINA CERAMICS BY THE CENTRIFUGAL CASTING METHOD