Alumina nanocrystalline ceramic by centrifugal casting
Yuanyuan Li,Bing Shen,Hongbing Yang,Guangkuo Hu,Desheng Yang,Jun Wang,Yanhao Dong,Jiangong Li
DOI: https://doi.org/10.1016/j.jeurceramsoc.2022.12.004
IF: 5.7
2022-12-17
Journal of the European Ceramic Society
Abstract:Centrifugal casting is an established molding method to prepare ceramics with high strength and high reliability and it has been well demonstrated in Al 2 O 3 . However, it has not yet been applied to Al 2 O 3 nanocrystalline ceramic with < 100 nm grain size, primarily due to the unavailability of high-quality α -Al 2 O 3 nanoparticles. In addition, ultrafine nanoparticles may be difficult to cast from the solution unless high-speed ultracentrifuge (e. g., >60,000 rpm) is used. Here we addressed these two challenges by home-made dispersed α -Al 2 O 3 nanoparticles with 10 nm average particle size and HCl-assisted casting under a "normal" centrifuge condition and report the first attempt to produce Al 2 O 3 nanocrystalline ceramic by centrifuge casting and pressureless sintering. The sintering kinetics and microstructure were analyzed, which assists the design of optimal two-step sintering schedule. We showed that dense Al 2 O 3 nanocrystalline ceramic with 65 nm average grain size and ultra-uniform microstructure (the standard deviation of the grain size distribution to the average grain size is 0.358) can be obtained by two-step sintering at 1175 °C without holding followed by holding at 1025 °C for 20 h. The ultra-uniform microstructure may result from the denser and more uniform packing of particles in the green bodies produced by centrifugal casting. The two-step sintered Al 2 O 3 nanocrystalline ceramic has a microhardness of 19.9 GPa. The microhardness indicates potential softening (inverse Hall-Petch relationship) of Al 2 O 3 nanocrystalline ceramic at such a grain size.
materials science, ceramics