Abstract:Porous yttria-stabilized zirconia (YSZ) ceramics were Prepared by tert-butyl alcohol (TBA)-based gel-casting with monodisperse polymethylmethacrylate (PMMA) microspheres (20 mu m) as both pore-forming agent and lubricant agent. The effects of content of PMMA on the pore size distribution, porosity, flexural strength and thermal conductivity of porous 8YSZ ceramics with TBA-based slurry of 50% (volume fraction) solid loading were investigated. The results show that the pores distribute homogeneously in the matrix with the pore size of 10 mu m and denser pore walls, and the porosity increases with increasing of amounts of PMMA in the slurry, the flexural strength decreases from 85.24 MPa to 61.89 MPa and the thermal conductivity changes from 1.108 W/m.K to 0.735 W/m.K when the porosity increases from 22.88% to 39.77%. It is shown that the additions of pore-forming agent during the gelcasting process can not only promote the preparation of porous ceramics with high solid loading, but also can make all the main factors controllable, such as the porosity, the size and shape of pores, the distribution of pores, and the thickness and density of pore walls, and thus the porous ceramics with both high strength and low thermal conductivity can be obtained.

Fabrication of porous alumina–zirconia ceramics by gel-casting and infiltration methods

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Preparation of porous ceramics by gelcasting approach

Controlled Fabrication of Porous Al2O3 Ceramic by N,N′-dimethylformamide-based Gel-Casting

Porous α-Al2O3 ceramics prepared by gelcasting

Fabrication of Porous Alumina Ceramics with Directional Pore Channels Structure by Freeze-Gel Casting Processing

Porous Yttria‐stabilized Zirconia Ceramics Fabricated by Nonaqueous‐Based Gelcasting Process with PMMA Microsphere As Pore‐Forming Agent

High-strength porous YSZ ceramics fabricated by TBA-based gelcasting with high solid loading slurry

Fabrication and Mechanical Properties of Homogeneous Zirconia Toughened Alumina Ceramics Via Cyclic Solution Infiltration and in Situ Precipitation

Air permeable alumina-based porous ceramics with high performance prepared by novel gel casting route

Fabrication of Porous Zirconia Ceramics by Injection Molding Method

Fabrication of Ceramics with Complex Porous Structures by the Impregnate–Freeze‐Casting Process

Ceramics with Special Porous Structures Fabricated by Freeze-Gelcasting: Using tert-Butyl Alcohol as a Template

A simple and efficient hydratable alumina gel‐casting method for the fabrication of high‐porosity mullite ceramics

Effects of Pore-Forming Agent Content on the Properties of Porous 8ysz Ceramics by Tba Based Gel-Casting

FABRICATION OF POROSITY GRADIENT ALUMINA CERAMICS BY THE CENTRIFUGAL CASTING METHOD

Fabrication of Low Density High Strength Porous Mullite Ceramics by Tert-Butyl Alcohol-Based Gelcasting Process

Fabrication, Structure and Properties of Porous SiC Ceramics with High Porosity and High Strength

Fabrication of Porous Ceramics with Unidirectionally Aligned Continuous Pores

A Novel Way to Fabricate Highly Porous Fibrous YSZ Ceramics with Improved Thermal and Mechanical Properties

Fabrication and Properties of Porous Yttria-Stabilized Zirconia Ceramics