IMPROVEMENT OF TOUGHENING AND MECHANICAL PROPERTIES EQUILIBRIUM FOR PA6/VERSIFY BLENDS BY VERSIFY-g-(MAH-co-St)

Zhang Jiamin,Li Yan,Xie Xuming

DOI: https://doi.org/10.3724/sp.j.1105.2009.00381

2009-01-01

Acta Polymerica Sinica

Abstract:A propylene-ethylene copolymer Versify2300 with 12 wt% ethylene content (V-2300) was multi-monomer melt grafted using maleic anhydride and styrene (MAH-St) by extruder. The effect of the addition of Versify-g-(MAH-co-St) (g-V-2300) on the compatibility of PA6/(V-2300 + g-V-2300) (70/30) blends was investigated by means of SEM, FTIR and mechanical property measurements. The results showed that with increasing the g-V-2300 content, the size of the V-2300 dispersed phase became smaller and more uniform. When g-V-2300 is 25 wt% the dispersed phase size is only 0.27 mu m, and the izod impact strength of the blend is 324.54 J/m and is 16 times larger than that of the blend without g-V-2300. The addition of g-V-2300 remarkably improved the mechanical properties of PA6/(V-2300 + g-V-2300) (70/30) blends including elongation, tensile strength and flexural strength. Thus toughened Nylon 6 alloys could be achieved with balanced mechanical properties.