Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

In Vitro Corrosion of Mg–1.21Li–1.12Ca–1Y Alloy

Comparison of Microstructure, Mechanical Property, and Degradation Rate of Mg–1Li–1Ca and Mg–4Li–1Ca Alloys

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Corrosion and Characterisation of Dual Phase Mg–Li–Ca Alloy in Hank’s Solution: the Influence of Microstructural Features

The Influence of Ca and Y on the Microstructure and Corrosion Resistance of Vacuum Die Casting AZ91 Alloy

Microstructure, mechanical properties and corrosion behavior of extruded Mg-Zn-Ca alloys with same Zn/Ca atomic ratio

Effect of minor Ca addition on microstructure and corrosion behavior of Mg–Y–Ca alloys

Microstructure and mechanical properties of as-cast ultralight and high strength Mg-10Li-3Al-3Zn-xY alloy with multi-precipitates

Effect of Ca Content on the Mechanical Properties and Corrosion Behaviors of Extruded Mg–7Li–3Al Alloys

Influence of Ultra-Fine Grain Structure on Corrosion Behaviour of Biodegradable Mg-1Ca Alloy

Effect of Microstructure on the Corrosion Behavior of as-cast and Extruded Mg–Sn–Y Alloys

Influence of mixed rare earth elements(Y and Ce) on the microstructure and corrosion behaviour of Mg-4Al-3Ca alloy

Effect of Y Contents on the Microstructure, Mechanical Properties, and Corrosion Behavior of Biomedical Mg‐0.5Zn Alloy

In Vitro Degradation and Biocompatibility of Mg-Li-Ca Alloys—the Influence of Li Content

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Effects of Y on Microstructure and Mechanical Properties of Extruded Mg-5Al-1Ca Magnesium Alloys

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Role of alloyed Al on the microstructure and corrosion behavior of as-cast dilute Mg-2Zn- x Al-0.5Ca alloys

Effect of YAl₂ Particles on the Corrosion Behavior of Mg⁻Li Matrix Composite in NaCl Solution

Effects of micro-alloying Ag on microstructure, mechanical properties and corrosion behavior of extruded Mg-2Zn-0.2Ca-xAg alloys