Abstract:Magnesium-zinc-calcium alloys have unique advantages of being used as biomedical bone implants since their mechanical properties and biocompatibility are similar to human tissues. However, insufficient strength and poor corrosion resistance have been the major problems to stunt the application. In this paper, the changes of microstructure, mechanical properties and corrosion resistance of ternary Mg-3Zn-0.2Ca (wt.%) with different contents of Mn (0.3, 0.5, 0.7, 0.9, wt.%) are studied. With the increase of Mn content, the grain size of as-cast alloy first decreases and then increases, this indicates that the amount of Mn affects the degree of subcooling of the alloy. At the 320°C/24 h homogenizing treatment, the large and uneven dendrites are transformed into uniform equiaxed grains, the mechanical properties of alloys with different Mn contents are different on the basis of Mg-3Zn-0.2Ca (wt.%) alloy. The five alloys were extruded into bar with a diameter of 8 mm through hot-extrusion process. Quaternary Mg-3Zn-0.2Ca-XMn (X = 0.3, 0.5, 0.7, 0.9) (wt.%) alloys are investigated and the results show that 0.5 wt.% Mn alloy has the best yield tensile strength (YS) (302 MPa) and good ultimate tensile strength (UTS) (327 MPa). The reason is that the different contents of Mn restrain the dynamic recrystallization in extrusion process, which remarkedly reduced the grain size. Moreover, each alloy is investigated by electrochemical measurements at 37°C in a simulated body fluid (SBF). The electrochemical results show that the corrosion potential of Mn-contained alloys are increased compared to ternary Mg-3Zn-0.2Ca (wt.%) alloy, and 0.5 wt.% Mn-contained alloy performs the best result.

Effect of Y Contents on the Microstructure, Mechanical Properties, and Corrosion Behavior of Biomedical Mg‐0.5Zn Alloy

Improvement of Mechanical Properties and Corrosion Resistance of As‐Extruded Mg–2Zn–2Al–0.3Mn Alloy Through Y Addition

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Effect of Y on Age Hardening Response and Mechanical Properties of Mg-xY–1.5LPC −0.4zr Alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effects of Y on Microstructure and Mechanical Properties of Extruded Mg-5Al-1Ca Magnesium Alloys

Effect of Y content on microstructure evolution and tensile properties of Mg-8Li-3Al-2Sn-xY alloys

Effect of Zn Content and Homogenization Treatment on Mechanical Properties and Corrosion Behavior of Mg-9Y-xZn Alloys

Effect of long period stacking ordered structure on the biocorrosion resistance and osteogenesis ability of Mg–Zn–Y-Mn alloys

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Role of Y on the microstructure and mechanical properties of Mg-Gd-Zr alloy

In vitro degradation behavior and biocompatibility of Mg–5.8 Zn–2.0 Yb–0.5 Zr alloy during aging treatment

Effect of Mn Element Addition on the Microstructure, Mechanical Properties, and Corrosion Properties of Mg-3Zn-0.2Ca Alloy

Effect of Microstructure on the Corrosion Behavior of as-cast and Extruded Mg–Sn–Y Alloys

Microstructure characterization and corrosion behavior of Mg–Y–Zn alloys with different long period stacking ordered structures

Effect of Extrusion on Mechanical Property, Corrosion Behavior, and In Vitro Biocompatibility of the As-Cast Mg-Zn-Y-Sr Alloy

Effect of Heat Treatment on Corrosion and Mechanical Properties of Mg-10Y-1.5Zn-0.5Zr Alloy

Comparative Study on Corrosion Behavior and Mechanism of As-Cast Mg–Zn–Y and Mg–Zn–Gd Alloys

Microstructure, Mechanical Properties and Corrosion Behavior of Mg-Zn-Zr Alloys with Different Compositions

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)

Effect of Zr content on the microstructure, mechanical properties, electrochemical behavior, and biocompatibility of Mg–3Zn–xZr alloy using powder metallurgy