Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Effect of Y content on microstructure evolution and tensile properties of Mg-8Li-3Al-2Sn-xY alloys

Microstructure and mechanical properties of as-cast ultralight and high strength Mg-10Li-3Al-3Zn-xY alloy with multi-precipitates

Effects of Y on Microstructure and Mechanical Properties of Extruded Mg-5Al-1Ca Magnesium Alloys

Effect of Sn content on microstructure and tensile properties of as-cast and as-extruded Mg−8Li−3Al−(1,2,3)Sn alloys

Simulation on Microstructure Evolution and Mechanical Properties of Mg−Y Alloys: Effect of Trace Y

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Effect of Al on Microstructure and Mechanical Properties of Mg-10Li-3Zn-1Y Alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effects of Li Content on Phase Evolution and Mechanical Properties of Mg-xLi-6Zn-1.5Y Alloy

Improvement of Mechanical Properties and Corrosion Resistance of As‐Extruded Mg–2Zn–2Al–0.3Mn Alloy Through Y Addition

Role of Y on the microstructure and mechanical properties of Mg-Gd-Zr alloy

Effect of yttrium addition on dynamic mechanical properties, microstructure, and fracture behavior of extrusion-shear ZC61 + xY (x = 0, 1, 2, 3) alloys

Microstructure and mechanical properties of Pb-40 Mg-10Al-1B-Y alloys

Effect of Yttrium Addition on Microstructure and Mechanical Properties of Sr-Modified Low-Si Cast Aluminum Alloy

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Effect of Al addition on the grain refinement and mechanical properties of as-cast Mg–5Y–4Sm alloys

Effect of Y Contents on the Microstructure, Mechanical Properties, and Corrosion Behavior of Biomedical Mg‐0.5Zn Alloy

The Effect of Y/Er and Zn Addition on the Microstructure and Mechanical Properties of Mg-11Li Alloy

Role of Y in High-Strength Mg–Y–Cu–Ni Alloy System with Long-Period Stacking Ordered Phase

Microstructure and Mechanical Properties of Extruded Mg-Zn-Nd-Y-Zr-Ca Alloy

Microstructure and mechanical properties of cast Mg-6Gd–Zr alloy with different Y addition