Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Role of Y in High-Strength Mg–Y–Cu–Ni Alloy System with Long-Period Stacking Ordered Phase

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Effect of Y content on microstructure evolution and tensile properties of Mg-8Li-3Al-2Sn-xY alloys

Simulation on Microstructure Evolution and Mechanical Properties of Mg−Y Alloys: Effect of Trace Y

Effect of Substituting Y with Gd on LPSO Phase Dispersion and Mechanical Properties of Mg-2Ni-2Y Alloy

Effects of Y on Microstructure and Mechanical Properties of Extruded Mg-5Al-1Ca Magnesium Alloys

Microstructure and mechanical properties of LPSO dominant Mg-2Y-Cu-TM (TM=Cu, Zn, Co, Ni) alloys

Role of Y on the microstructure and mechanical properties of Mg-Gd-Zr alloy

Effect of the Morphology of Long-Period Stacking Ordered Phase on Mechanical Properties and Corrosion Behavior of Cast Mg-Zn-Y-Ti Alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effect of Y on Age Hardening Response and Mechanical Properties of Mg-xY–1.5LPC −0.4zr Alloys

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Improved hardness of Mg-0.5Ni- x Y alloys via grain refinement and formation of LPSO structures

Effect of Y on microstructure, damping properties and mechanical properties of Cu-Al-Ni-Mn alloy

Enhancing the strain hardening and ductility of Mg-Y alloy by introducing stacking faults

Microstructure and mechanical properties of as-cast ultralight and high strength Mg-10Li-3Al-3Zn-xY alloy with multi-precipitates

Microstructure and mechanical properties of Cu-Ni-Sn alloy regulated by trace rare earth element Y

Improvement of Mechanical Properties and Corrosion Resistance of As‐Extruded Mg–2Zn–2Al–0.3Mn Alloy Through Y Addition

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Strength-ductility synergy in Mg98.3Y1.3Ni0.4 alloy processed by high temperature homogenization and rolling