Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Microstructure and mechanical properties of LPSO dominant Mg-2Y-Cu-TM (TM=Cu, Zn, Co, Ni) alloys

Effect of the Morphology of Long-Period Stacking Ordered Phase on Mechanical Properties and Corrosion Behavior of Cast Mg-Zn-Y-Ti Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructure Evolution and Mechanical Properties of Mg-LPSO Two Phase Mg96Y2Ni2 (at. %) Alloy Processed by Hot Extrusion and Decreasing-Temperature ECAP

Microstructure and Mechanical Properties of Mg–9RY–4Cu Alloy with Long Period Stacking Ordered Phase

Improved Strength in Wrought Mg–Y–Ni Alloys by Adjusting the Block-Shaped LPSO Phase and Plate-Shaped Γ′ Phase

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Deformation Behavior of Mg-Y-Ni Alloys Containing Different Volume Fraction of LPSO Phase During Tension and Compression Through In-Situ Synchrotron Diffraction

Role of Cu on the Mechanical Properties and Microstructures Evolution of Al-xCu-1Li-0.4Mg–1Zn-0.1Zr Alloys

Understanding the High Strength and Good Ductility in LPSO-Containing Mg Alloy Using Synchrotron X-ray Diffraction

In-situ investigate on the microstructure evolution, deformation and fracture mechanism of Mg-Gd-Zn-Mn alloy with varies of LPSO volume fraction

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Microstructure and yield phenomenon of an extruded Mg-Y-Cu alloy with LPSO phase

Effect of ultrasonic vibration on microstructure and mechanical properties of Mg98Y1.0Ni0.5Al0.5 alloy containing LPSO structure

Microstructures and Mechanical Properties of Hot-extruded Mg-6Zn-xCu-0.6Zr(x=0,0.5,1.0,1.5) Alloys

Effect of Al element on microstructure, mechanical properties and damping capacity of LPSO-containing Mg-Y-Zn-Li alloy

Role of Y in High-Strength Mg–Y–Cu–Ni Alloy System with Long-Period Stacking Ordered Phase

Effect of Volume Fraction of LPSO Phases on Corrosion and Mechanical Properties of Mg-Zn-Y Alloys

Strength-ductility synergy in Mg98.3Y1.3Ni0.4 alloy processed by high temperature homogenization and rolling

Unveiling the strengthening effect of LPSO phase in a Mg-Y-Zn alloy

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy