Abstract:Annealing Mg-implanted homoepitaxial GaN at temperatures above 1400 °C eliminates the formation of inversion domains and leads to improved dopant activation efficiency. Extended defects, in the form of inversion domains, contain electrically inactive Mg after post-implantation annealing at temperatures as high as 1300 °C (one GPa N2 overpressure), which results in a low dopant activation efficiency. Triple-axis x-ray data reveal that implant-induced strain is fully relieved after annealing at 1300 °C for 10 min, indicating that strain-inducing point defects formed during implantation have reconfigured and inversion domains are formed. However, annealing at temperatures of 1400–1500 °C (one GPa N2 overpressure) eliminates the presence of the inversion domains. While residual defects, such as dislocation loops, still exist after annealing at and above 1400 °C, chemical analysis at multiple dislocation loops shows no sign of Mg segregation. Meanwhile, an overall decreasing trend in the dislocation loop density is observed after annealing at the higher temperatures and longer times. Additionally, once inversion domains are formed and the samples are cooled to room temperature, they are shown to dissolve with subsequent annealing above 1400 °C. While such defects have been observed before, the important finding that such defects can be dissolved with a short, higher temperature step is key. Earlier work [Breckenridge et al., J. Appl. Phys. Lett. 118, 022101 (2021)] addressing electrical measurements of these types of samples showed that annealing at 1400 °C leads to a dopant activation efficiency that is an order of magnitude higher than that observed at 1300 °C. This work complements earlier work by identifying the inversion domains, which incorporate Mg, and points to the benefits, in terms of defect density and p-type dopant activation, of using higher temperature (>1400 °C) annealing cycles to activate Mg in GaN, even if the Mg-containing inversion domains had been formed during lower temperature annealing.

Non-Equilibrium Acceptor Concentration in Gan : Mg Grown by Metalorganic Chemical Vapor Deposition

Growth and fabrication of GaN/AlGaN heterojunction bipolar transistor

High Mg activation in implanted GaN by high temperature and ultrahigh pressure annealing

Defects in GaN Films Studied by Positron Annihilation Spectroscopy

Influence of High Mg Doping on the Microstructural and Opto-Electrical Properties of AlGaN Alloys

Mg acceptors activation mechanism and hole transport characteristics in highly Mg-doped AlGaN alloys

Dissolution of Mg-enriched defects in implanted GaN and increased p-type dopant activation

(Invited) Understanding Mg-Related Defects for Vertical GaN p-n Junction Structures Via p-Type Ion Implantation

Depth Analyses of Mg‐Acceptor and Si‐Donor Concentrations in GaN by Combining Stepwise Etching and Photoluminescence

Ni Diffusion and Its Influence on Electrical Properties of AlxGa1−xN∕GaN Heterostructures

P-Type Gan Directly Grown by Low Pressure Metalorganic Vapor Phase Epitaxy

Study of the heavily p-type doping of cubic GaN with Mg

The Influence of Indium Surfactant on the Electrical Properties of GaN Epilayers Grown by Metal-Organic Chemical Vapour Deposition

Highly effective activation of Mg-implanted p-type GaN by ultra-high-pressure annealing

Incorporation of Magnesium into GaN Regulated by Intentionally Large Amounts of Hydrogen during Growth by MOCVD

Formation of Grown-In Nitrogen Vacancies and Interstitials in Highly Mg-Doped Ammonothermal GaN

P-Type Doping Of Gan By Mg+ Implantation

Properties of Mg-Doped AlGaN Films

MOCVD growth and annealing characteristics of Mg-doped AlGaN films

Study on Mg-doped AlGaN Films Grown by Metal Organic Chemical Vapor Deposition

Self-compensation due to point defects in Mg-doped GaN