The Characters of Mo-Mosi2 Functionally Graded Coating

Ying-Yi Zhang,Yun-Gang Li,Yuan-Hong Qi,Zong-Shu Zou

DOI: https://doi.org/10.1515/htmp-2013-0046

2014-01-01

High Temperature Materials and Processes

Abstract:Mo-MoSi2 functionally graded coating on Mo substrate is prepared by siliconizing technology. The characters of Mo-MoSi2 functionally graded coating are analyzed by SEM, EDS, GDS and XRD. The result shows that Mo-MoSi2 functionally graded coating is dense and smooth, without pore and crack defects, gradient coating and Mo matrix achieve good metallurgy bond. The silicon molybdenum atom ratios (Si/Mo) in functionally graded coating appear three changing regularities. When the Si/Mo of outer layer are from 6: 1 to 2: 1, the surface phase is constituted by MoSi2 and Si; when the Si/Mo of interlayer is about 2: 1, the interlayer phase is constituted by MoSi2; when the Si/Mo of transitional layer are from 2: 1 to 0: 1, the transitional layer phase is constituted by Mo5Si3 and Mo. The phase structure of Mo-MoSi2 functionally graded coating from outside to inside is outer layer MoSi2+Si, interlayer MoSi2 and transitional layer Mo5Si3+Mo3Si three-layer structure. The thermodynamic calculation results are consistent with the experimental results substantially.