Abstract:La2Zr2O7 (LZO) buffer layers were deposited on bi-axially textured Ni–W substrates with CeO2 seed layer by radio-frequency magnetron sputtering for the large-scale application of YBa2Cu3O7−x (YBCO) coated conductors. The microstructure and surface morphology of LZO buffer layers were studied by X-ray diffraction, optical microscopy, field emission scanning electron microscopy and atomic force microscopy. The influences of substrate temperature and oxygen partial pressure on the microstructure and surface morphology of LZO buffer layers were discussed. It was found that epitaxial LZO films were preferentially c-axis oriented without microcracks, with no degradation of crystallographic texture and with high surface crystallinity. Crack-free and strong c-axis aligned LZO films with no random orientation were obtained at relatively low substrate temperatures of 600–800°C and in flowing 40Pa gas mixtures of Ar–O2 with an effective oxygen partial pressure of 0.1–20Pa. In addition, LZO films grown in low oxygen partial pressure have a smoother surface than films in higher oxygen partial pressure. Then, we fabricated YBCO coated conductors on the high-quality LZO buffer layers by pulsed laser deposition. The critical current density Jc=2.25MA/cm2 and critical current Ic=180A/cm of 0.8-μm-thick YBCO film at 77K, self field were obtained. The magnetic field and angular dependences of critical current per width were discussed. Highly textured LZO films grown on CeO2 seed layer were suitable as a buffer layer for the growth of YBCO coated conductors with high currents.

Fabrication and Characterization of La2Zr2O7 Films on Different Buffer Architectures for YBa2Cu3O7−δ Coated Conductors by RF Magnetron Sputtering

Improved Textured La2Zr2O7 Buffer Layers on Bi-Axially Textured Ni–W Substrates Using CeO2 Seed Layers for YBa2Cu3O7−x Coated Conductors

Growth of Thick La2Zr2O7 Buffer Layers for Coated Conductors by Polymer-Assisted Chemical Solution Deposition

Metal Organic Deposition of Lanthanum Zirconate Buffer Layer on Biaxially Textured Ni-5%W Substrate

Tailoring the Crystallographic Orientation of MOD-derived La2Zr2O7 Buffer Layers for Coated Conductors

Reel-To-Reel Continuous Deposition Of Ce(X)Zr(1-X)O(2) Single Buffer Layer For Ybco Coated Conductors

Single Cerium Zirconate Buffer Layer on Biaxially Textured Metal Substrates for High Performance Coated Conductors

Reel-To-Reel Deposition of Epitaxial Double-Sided Y2o3 Buffer Layers for Coated Conductors

A Compositional Gradient Ce1−xZrxO2 Buffer Architecture for Producing High-Performance YBCO Film

Preparation and Characterization of Ceo2/Ysz/Ceo2 Buffer Layers for Ybco Coated Conductors

Epitaxial growth of Gd 2 Zr 2 O 7 /Y 2 O 3 buffer layers for YBa 2 Cu 3 O 7− δ coated conductors

Microstructure Analysis of High-Quality Buffer Layers on Textured Niw Tapes for Ybco Coated Conductors

Uniformity of Long-Length Double-Sided CeO_2 Buffer Layer for YBa_2Cu_3O_(7-δ) Coated Conductors

Simultaneous double-sided deposition of long-length epitaxial CeO 2 buffer layers for YBCO coated conductors

Polymer-assisted Chemical Solution Deposition of High-Quality La2Zr2O7 Buffer Layer Applied to Low-Cost YBCO-coated Conductors

Preparation of Biaxially Textured Ce1-x(Y0.2Zr0.8)xOδ Buffer Layers on RABiTS NiW Tapes by Chemical Solution Deposition

Fabrication of YBCO Coated Conductors on Biaxial Textured Metal Substrate by All-Sputtering

Thickness Effect of Gd2Zr2O7 Buffer Layer on Performance of YBa2Cu3O7−δ Coated Conductors

Texture and Morphology Developments of Yttria-stabilized Zirconia (YSZ) Buffer Layer for Coated Conductors by RF Sputtering

Fabrication of Long Length Baseband of Buffer layer of Metal Organic Deposited Coating conductor La 2 Zr 2 O 7

Growth of Simplified Buffer Template on Flexible Metallic Substrates for YBa2Cu3O Coated Conductors