Abstract:Core-shell structured SiC/SiO2 nanowires (SiC/SiO2 NWs) were synthesized by a simple thermal evaporation method without a catalyst. The influence of the growth temperature and holding time on the microstructure and composition of the nanowires were investigated. The results indicate that within the temperature range of 1150 to 1550 degrees C, the color of SiC/SiO2 nanowires gradually transitions from pure white to off-white with increasing temperature. During this process, the average diameter of SiC/SiO2 increases from 74 nm to 291 nm, while the surface SiO2 layer thickness decreases from 17 nm to 5 nm, with nanowires can reach lengths of hundreds of micrometres. Variations in supersaturation of SiO and CO at different temperatures lead to discrepancies in nanowire diameter and SiO2 shell thickness. At 1350 degrees C, prolonged holding time enhances silicon powder reaction, resulting in increased structural disorder of the obtained SiC/SiO2 nanowires. The nanowire growth follows a vapor-solid (V-S) mechanism. Additionally, the study demonstrates that the photoluminescence (PL) characteristics of the nanowires exhibit a blue shift attributable to their nanoscale dimensions, while variations in emission spectra correlate with stacking faults, SiC diameter, and SiO2 thickness. This work may be provide a theoretical basis for preparing SiC/SiO2 nanowires with different diameters and SiO2 shell thicknesses, which is crucial for advancing the development and application of SiC/SiO2 nanoceramics.

A Simple Route to Growth of Silicon Nanowires

Ultrafast growth of single-crystalline Si nanowires

Silicon Nano-Wires Fabricated by Thermal Evaporation of Silicon Wafer

A Novel Sulfide-Assisted Growth of Silicon Nano-Wires

Sulfide-assisted Growth of Silicon Nano-Wires by Thermal Evaporation of Sulfur Powders

Silicon Nano-Wires Fabricated by a Novel Thermal Evaporation of Zinc Sulfide

From powder to nanowire: A simple and environmentally friendly strategy for optical and electrical GaN nanowire films

A Novel Approach To Silicon-Nanowire-Assisted Growth Of High-Purity, Single-Crystalline Beta-Si3n4 Nanowires

1.5 Μm Luminescence of Silicon Nanowires Fabricated by Thermal Evaporation of SiO

Light emission from as-prepared and oxidized Si nanowires with diameters of 5–15 nm

Guided Growth of In-Plane Silicon Nanowires

A New Route to Large‐Scale Synthesis of Silicon Nanowires in Ultrahigh Vacuum

Growth of SiC Nanowires from NiSi Solution

The Growth Mechanism of Silicon Nanowires and Their Quantum Confinement Effect

Silicon Nanowires Grown from Au-coated Si Substrate

Catalytic Synthesis and Growth Mechanism of SiC@SiO2 Nanowires and Their Photoluminescence Properties

A simple route to synthesize scales of aligned single-crystalline SiC nanowires arrays with very small diameter and optical properties.

Preparation of Photoluminescent Silicon Nanowires Based on Multicrystalline Silicon Wafers

Growth of Silicon Nanowires by Heating Si Substrate

In-situ Synthesis of SiC/SiO2 Nanowires by Catalyst-Free Thermal Evaporation of Silicon Powder and Their Photoluminescence Properties

Synthesis and Photoluminescence Properties of Porous Silicon Nanowire Arrays