Abstract:Composite of copper and 3 mol% yttria-stabilized 5 wt.% zirconia (3-YSZ) have been prepared by hydrogen (PH2=0.1atm) reduction of a homogeneous mixture of equably dispersed CuO and ZrO2 formed by three chemical processes. In these processes, the 5%ZrO2/Cu nano-composite has been formed in situ by (1) addition of NaOH solution to certain amount of dispersed Cu(NO3)2, ZrOCl2 and Y(NO3)3 alcohol solution, following filtration; or (2) by adding ammonia to ZrOCl2, Y(NO3)3 solution, then adding Cu(NO3)2 solution to the deposition; (3) the mixture of Zr(OH)4 and Cu(NO3)2·3H2O, mixing and heating the final composition in the three cases to acquire the blending. And calcined them at 500 °C for 1 h. The 5%ZrO2/Cu composites were fabricated by quenching and final sintering at 900 °C for 90 min in vacuum atmosphere. The three process were named process A, process B, and process C. The characterization of the composite samples has been done by XRD, SEM, TEM and metallography techniques. Results from XRD and TEM indicated that different crystal structure zirconia was formed in the three processes. In comparison, the composite microstructure of process B was more homogenous. The comparative conductivity and Vickers hardness were 64% IACS and 120, which were much higher than the other two processes.

In Situ Synthesis Of Nano-Sized Zrc And Its Formation Mechanism By Combustion Synthesis From Zr-C-Cu System

Study of Formation Behavior of ZrC in the Cu–Zr–C System During Combustion Synthesis

ZrC/Cu composites in situ fabricated by self-propagating high-temperature synthesis in Cu-Zr-C system

Kinetic Role of Cu Content in Reaction Process, Behavior and Their Relationship among Cu-Zr-C System

Nano-sized Amorphous Cu–Zr Alloy Particles Prepared by Mechanochemical Reaction

Reaction Synthesis Of Nano-Scale Zrc Particulates By Self-Propagating High-Temperature Synthesis From Al-Zr-C Powder Mixtures

Combustion and formation behavior of hybrid ZrB 2 and ZrC particles in Al-Zr-B 4C system during self-propagation high temperature synthesis

Preparation and microstructure of nano-sized Cu particles by mechanochemical reaction

In situ synthesis of ZrC particles and its formation mechanism by self-propagating reaction from Al–Zr–C elemental powders

Nanostructured Hybrid Carbon Nanotube/UltraHigh‐Temperature Ceramic Heterostructures: Microstructure Evolution and Forming Mechanism

Combinatorial synthesis of multiple Zr Ti1-C by electric field-assisted combustion synthesis

Combustion synthesis and characterization of NiCuZn ferrite powders

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Nanomaterials Via Solution Combustion Synthesis: a Step Nearer to Controllability

In Situ Formation of Cu–ZrO2 Composites by Chemical Routes

A Co-reduction-carburization Route to Synthesize Nanocrystalline ZrC

Reaction Behavior and Formation Mechanism of ZrB2 and ZrC from the Ni-Zr-B4C System during Self-Propagating High-Temperature Synthesis

In Situ Synthesis, Mechanical Properties, and Oxidation Resistance of (sic+zrb2)/zr3[al(si)]4c6 Composites

In-Situ Fabrication of ZrB2-ZrC-SiCnws Hybrid Nanopowders With Tunable Morphologies of SiCnws

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Preparation of ZrB2-ZrC-SiC-ZrO2 nanopowders with in-situ grown homogeneously dispersed SiC nanowires