Abstract:This paper investigates the deterioration of, and the abnormal temperature rise in, the GFRP core rod material of compact V-string composite insulators subjected to prolonged alternating flexural loading under wind-induced stresses. The axial stress on the GFRP (Glass Fiber Reinforced Plastic) core rod, resulting from transverse wind loads, is a focal point of examination. By establishing a stress model and damage model, the paper simulates and computes the evolution of damage in the outer arc material of composite insulator core rods subjected to alternating flexural loads. Additionally, a multi-factor coupled aging platform is set up, integrating humidity, heat, and mechanical stress, to simulate the crazing deterioration process of composite insulators under alternating flexural loads. Experimental results reveal that during 400,000 alternating load cycles, the core rod underwent stages of surface damage, damage increasing, fatigue embrittlement, matrix hydrolysis, and fiber fracture. Simultaneously, the silicone rubber sheath on the outer side of the composite insulator's bending arc develops cracks over aging time, creating pathways for moisture ingress into the interface and core rod. The dielectric constant and dielectric loss factor of the aging region of the core rod increase to varying degrees compared to the non-aging part. Moreover, the degree of abnormal heating of the samples intensifies with the duration of aging experiments. These findings underscore the significance of understanding the aging and decay-like fracture process of compact line V-string composite insulators. They provide crucial insights for future research aimed at enhancing the material properties of composite insulator core rods.

Mechanical Performance of In-service Composite Insulators

Review in Application of High Voltage Composite Insulator and Its Ageing State

Mechanical Reliability of Crimped Composite Insulators with High Specified Mechanical Load in Long-term Service

Study on the Aging Characteristics of a ±500 kV Composite Dead-End Insulator in Longtime Service

Analysis of a Fractured 500 Kv Composite Insulator - Identification of Aging Mechanisms and Their Causes

Artificial Aging Tests with Defective Composite Insulators

Study on the Mechanism Effect of Bending Loads on the Decay-like Degradation of Composite Insulator GFRP Core Rod

Non-destructive Condition Assessment of Silicone Rubber Composite Insulators

Influence of Surface Discharge on Resin Degradation in Decay-like Fracture of Composite Insulators.

Study on electrical properties and field solutions of water related heating of composite insulators on 500kV AC transmission lines

Fatigue Fracture of Composite Insulator Sheds Utilized in Strong Wind Areas

Condition Assessment Strategies of Composite Insulator Based on Statistic Methods

Experimental and Numerical Study on Failure Behaviors of Composite Grid Stiffeners under Tensile and Flexural Loading

Application and Key Technical Study of Composite Insulators

Fracture Fault Analysis and Aging Mechanism Study for 500 kV Composite Insulator

A new method of 5 000 h artificial accelerating ageing test for composite insulator

Fatigue Damage Analysis of Composite Insulator Cor Rod/sheath Interface

Development History and Direction of Composite Insulators on Important Manufacture Technique

Reliability of Composite Insulators Used for UHV AC/DC Transmission Line

Simulation of Composite Insulator Interface Defects in Partial Discharge

Study on Deterioration Characteristics of a Composite Crossarm Mandrel in a 10 kV Distribution Network Based on Multi-Factor Aging