Study on the Mechanism Effect of Bending Loads on the Decay-like Degradation of Composite Insulator GFRP Core Rod

Xiaoyu Yi,Likun Ding,Hongliang Liu,Jiaxin Zhang,Jie Liu,Zhaohui Li,Yuming Zhang,Ping Wang,Jianghai Geng

DOI: https://doi.org/10.3390/en17020423

IF: 3.2

2024-01-15

Energies

Abstract:This paper investigates the deterioration of, and the abnormal temperature rise in, the GFRP core rod material of compact V-string composite insulators subjected to prolonged alternating flexural loading under wind-induced stresses. The axial stress on the GFRP (Glass Fiber Reinforced Plastic) core rod, resulting from transverse wind loads, is a focal point of examination. By establishing a stress model and damage model, the paper simulates and computes the evolution of damage in the outer arc material of composite insulator core rods subjected to alternating flexural loads. Additionally, a multi-factor coupled aging platform is set up, integrating humidity, heat, and mechanical stress, to simulate the crazing deterioration process of composite insulators under alternating flexural loads. Experimental results reveal that during 400,000 alternating load cycles, the core rod underwent stages of surface damage, damage increasing, fatigue embrittlement, matrix hydrolysis, and fiber fracture. Simultaneously, the silicone rubber sheath on the outer side of the composite insulator's bending arc develops cracks over aging time, creating pathways for moisture ingress into the interface and core rod. The dielectric constant and dielectric loss factor of the aging region of the core rod increase to varying degrees compared to the non-aging part. Moreover, the degree of abnormal heating of the samples intensifies with the duration of aging experiments. These findings underscore the significance of understanding the aging and decay-like fracture process of compact line V-string composite insulators. They provide crucial insights for future research aimed at enhancing the material properties of composite insulator core rods.

energy & fuels

What problem does this paper attempt to address?

The paper attempts to address the issue of the degradation and abnormal temperature rise phenomenon of glass fiber reinforced plastic (GFRP) core rod materials in composite insulators under long-term wind-induced alternating bending loads. Specifically, the paper focuses on:

1. **Degradation mechanism of GFRP core rod materials**: Investigating the damage evolution process of GFRP core rod materials under alternating bending loads, particularly stages such as surface damage, damage accumulation, fatigue embrittlement, matrix hydrolysis, and fiber breakage.

2. **Aging cracks in the silicone rubber sheath**: Exploring the development process of aging cracks on the outer bending arc of the silicone rubber sheath, which form channels for moisture ingress to the interface and core rod.

3. **Changes in dielectric constant and dielectric loss factor**: Analyzing the changes in dielectric constant and dielectric loss factor in the aging region compared to the non-aging part.

4. **Abnormal temperature rise phenomenon**: Studying the abnormal temperature rise phenomenon of samples during aging experiments and its aggravation with aging time.

By establishing stress and damage models, the damage evolution process of the composite insulator core rod under alternating bending loads on the outer bending arc material is simulated and calculated. Additionally, a multi-factor coupled aging platform was established, combining humidity, temperature, and mechanical stress to simulate the crack degradation process of composite insulators under alternating bending loads. These research results are of great significance for understanding the aging and decay-like fracture process of compact V-string composite insulators and provide valuable insights for future research to improve the performance of composite insulator core rod materials.